Polyethylene blend compositions and film

ABSTRACT

A polymer blend comprising first and second polyethylene copolymers is presented which has good processability, and which when made into film shows good toughness-stiffness balance, reasonable MD tear, as well as good optical properties.

FIELD OF THE INVENTION

A polymer blend having good processability, good toughness-stiffnessbalance, and which shows good optical properties when made into films ispresented. A polymer blend comprises from about 5 to about 95 wt % of afirst polyethylene copolymer having a density of from about 0.916 toabout 0.936 g/cm³, a melt index (I₂) of from about 0.1 to about 2.0 g/10min, a melt flow ratio (I₂₁/I₂) of from about 32 to about 50, amolecular weight distribution (M_(w)/M_(n)) of from about 3.6 to about6.5, a reverse comonomer distribution profile as determined by GPC-FTIR,a multimodal TREF profile, and a composition distribution breadth indexCDBI₅₀ of from about 45 to about 75 wt % as determined by TREF; andwhich satisfies at least one of the following relationships:(M _(w) /M _(n))≧72[(I ₂₁ /I ₂)⁻¹+10⁻⁶(M _(n))];δ^(XO) of from 55° to 70°;δ^(XO)≦83.0−1.25(CDBI₅₀)/(M _(w) /M _(n)); orδ^(XO)≦80.7−(CBDI₅₀)/(M _(w) /M _(n)) at a δ^(XO) of from 55° to 70°.

The balance of the polymer blend comprises a second polyethylenecopolymer which is different from the first polyethylene copolymer.

BACKGROUND OF THE INVENTION

The search for polyethylene products having an improved balance ofphysical properties and processability has led to the development ofproducts having improved output capacity and ever improving end useproperties such as enhanced film tear or dart impact properties.

In co-pending CA Pat. Appl. No. 2,734,167, we showed that suitablysubstituted phosphinimine catalysts gave narrow molecular weightdistribution copolymers which when made into film showed a good balanceof optical and physical properties.

Polymers and films made in the gas phase using various single sitecatalysts, including so called “phosphinimine” catalysts, were disclosedat Advances in Polyolefins II, Napa, Calif.—Oct. 24-27, 1999(“Development of NOVA's Single Site Catalyst Technology for use in theGas Phase Process”—I. Coulter; D. Jeremic; A. Kazakov; I. McKay).

In a disclosure made at the 2002 Canadian Society for ChemistryConference (“Cyclopentadienyl Phosphinimine TitaniumCatalysts—Structure, Activity and Product Relationships in HeterogeneousOlefin Polymerization.” R. P. Spence; I. McKay; C. Carter; L. Koch; D.Jeremic; J. Muir; A. Kazakov. NOVA Research and Technology Center, CIC,2002), it was shown that phosphinimine catalysts bearing variouslysubstituted cyclopentadienyl and indenyl ligands were active toward thegas phase polymerization of ethylene when in supported form.

There is still potential for new blend compositions exhibiting a goodbalance of physical properties and good processability.

SUMMARY OF INVENTION

Provided are polymer blends having good processability, goodtoughness-stiffness balance, and which show good optical properties whenmade into films.

Provided is a polymer blend comprising a polyethylene copolymer having adensity of from about 0.916 to about 0.936 g/cm³, a melt index (I₂) offrom about 0.1 to about 2.0 g/10 min, a melt flow ratio (I₂₁/I₂) of fromabout 32 to about 50, a molecular weight distribution (M_(w)/M_(n)) offrom about 3.6 to about 6.5, a reverse comonomer distribution profile asdetermined by GPC-FTIR, a multimodal TREF profile, a compositiondistribution breadth index CDBI₅₀ of from about 45 wt % to about 75 wt %as determined by TREF and which satisfies at least one of the followingrelationships:(M _(w) /M _(n))≧72[(I ₂₁ /I ₂)⁻¹+10⁻⁶(M _(n))];δ^(XO) of from 55° to 70°;δ^(XO)≦83.0−1.25(CDBI₅₀)/(M _(w) /M _(n)); orδ^(XO)≦80.7−(CDBI₅₀)/(M _(w) /M _(n)) at a δ^(XO) of from 55° to 70°.

Provided is a polymer blend comprising from about 5 to about 99 wt %based on the total weight of the polymer blend, of a polyethylenecopolymer having a density of from about 0.916 to about 0.936 g/cm³, amelt index (I₂) of from about 0.1 to about 2.0 g/10 min, a melt flowratio (I₂₁/I₂) of from about 32 to about 50, a molecular weightdistribution (M_(w)/M_(n)) of from about 3.6 to about 6.5, a reversecomonomer distribution profile as determined by GPC-FTIR, a multimodalTREF profile, a composition distribution breadth index CDBI₅₀ of fromabout 45 wt % to about 75 wt % as determined by TREF and which satisfiesat least one of the following relationships:(M _(w) /M _(n))≧72[(I ₂₁ /I ₂)⁻¹+10⁻⁶(M _(n))];δ^(XO) of from 55° to 70°;δ^(XO)≦83.0−1.25(CDBI₅₀)/(M _(w) /M _(n)); orδ^(XO)≦80.7−(CDBI₅₀)/(M _(w) /M _(n)) at a δ^(XO) of from 55° to 70°.

Provided is a polymer blend comprising: a) from about 5 to about 95 wt %of a first polyethylene copolymer having a density of from about 0.916to about 0.936 g/cm³, a melt index (I₂) of from about 0.1 to about 2.0g/10 min, a melt flow ratio (I₂₁/I₂) of from about 32 to about 50, amolecular weight distribution (M_(w)/M_(n)) of from about 3.6 to about6.5, a reverse comonomer distribution profile as determined by GPC-FTIR,a multimodal TREF profile, a composition distribution breadth indexCDBI₅₀ of from about 45 wt % to about 75 wt % as determined by TREF andwhich further satisfies the relationship: (M_(w)/M_(n))≧72[(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))]; and b) from about 95 to about 5 wt % of asecond polyethylene copolymer which is a linear low density polyethylene(LLDPE) different from the first polyethylene copolymer and having adensity of from about 0.910 to about 0.940 g/cm³, a melt index (I₂) offrom about 0.2 to about 5.0 g/10 min, and a melt flow ratio (I₂₁/I₂) ofless than about 35.

Provided is a polymer blend comprising: a) from about 5 to about 95 wt %of a first polyethylene copolymer having a density of from about 0.916to about 0.936 g/cm³, a melt index (I₂) of from about 0.1 to about 1.0g/10 min, a melt flow ratio (I₂₁/I₂) of from about 32 to about 50, amolecular weight distribution (M_(w)/M_(n)) of from about 3.6 to about6.5, a reverse comonomer distribution profile as determined by GPC-FTIR,a multimodal TREF profile, a composition distribution breadth indexCDBI₅₀ of from about 45 wt % to about 75 wt % as determined by TREF andwhich further satisfies the relationship: (M_(w)/M_(n))≧72[(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))]; and b) from about 95 to about 5 wt % of asecond polyethylene copolymer which is a linear low density polyethylene(LLDPE) having a density of from about 0.910 to about 0.940 g/cm³, amelt index (I₂) of from about 0.2 to about 5.0 g/10 min, and a melt flowratio (I₂₁/I₂) of less than about 32.

Provided is a polymer blend comprising: a) from about 5 to about 95 wt %of a first polyethylene copolymer having a density of from about 0.916to about 0.936 g/cm³, a melt index (I₂) of from about 0.1 to about 1.0g/10 min, a melt flow ratio (I₂₁/I₂) of at least about 30, a molecularweight distribution (M_(w)/M_(n)) of from about 3.6 to about 6.5, areverse comonomer distribution profile as determined by GPC-FTIR, amultimodal TREF profile, a composition distribution breadth index CDBI₅₀of from about 45 wt % to about 75 wt % as determined by TREF and whichfurther satisfies the relationship: (M_(w)/M_(n))≧72 [(I₂₁/I₂)⁻¹+10⁻⁶(M_(n))]; and b) from about 95 to about 5 wt % of a second polyethylenecopolymer which is a linear low density polyethylene (LLDPE) having adensity of from about 0.910 to about 0.940 g/cm³, a melt index (I₂) offrom about 0.2 to about 5.0 g/10 min, and a melt flow ratio (I₂₁/I₂) ofless than about 35.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1A shows a temperature rising elution fractionation (TREF) analysisand profile of a first polyethylene copolymer used according to thepresent invention.

FIG. 1B shows a temperature rising elution fractionation (TREF) analysisand profile of a first polyethylene copolymer used according to thepresent invention.

FIG. 2 shows a gel permeation chromatograph (GPC) with refractive indexdetection, of a first polyethylene copolymer used according to thepresent invention.

FIG. 3 shows a gel permeation chromatograph with Fourier transforminfra-red (GPC-FTIR) detection obtained for a first polyethylenecopolymer made according to the present invention. The comonomercontent, shown as the number of short chain branches per 1000 carbons(y-axis), is given relative to the copolymer molecular weight (x-axis).The upwardly sloping line (from left to right) is the short chainbranching (in short chain branches per 1000 carbons atoms) determined byFTIR. As can be seen in the Figure, the number of short chain branchesincreases at higher molecular weights, and hence the comonomerincorporation is said to be “reversed”.

FIG. 4A show plots of the phase angle vs the complex modulus and thephase angle vs. complex viscosity for resins 2A and 2B as determined bydynamic mechanical analysis (DMA).

FIG. 4B show plots of the phase angle vs the complex modulus and thephase angle vs. complex viscosity for resin 1A as determined by DMA.

FIG. 5 shows a plot of the equation: Mw/Mn=72 [(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))].The values from the equation 72 [(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))] (the y-axis)are plotted against the corresponding Mw/Mn values (the x-axis) forresins 1A-1F as well as for several commercially available resins whichhave a melt index I₂ of 1.5 g/10 min or less and a density of between0.916 and 0.930 g/cm³.

FIG. 6 shows a plot of the equation: δ^(XO)=83−1.25(CDBI₅₀)/(M_(w)/M_(n)). The values of the equation 80−1.25(CDBI₅₀/(M_(w)/M_(n)) (the x-axis) are plotted against the correspondingcrossover phase angle on values (the y-axis) for resins 1A-1F as well asfor several commercially available resins which have a melt index I₂ of1.5 g/10 min or less and a density of between 0.916 and 0.930 g/cm³.

FIG. 7 shows a plot of the equation: δ^(XO)=80.7−(CDBI₅₀)/(M_(w)/M_(n)).The values of the equation 80.7−(CDBI₅₀)/(M_(w)/M_(n)) (the x-axis) areplotted against the corresponding crossover phase angle (δ^(XO)) values(the y-axis) for resins 1A-1F as well as for several commerciallyavailable resins which have a melt index I₂ of 1.5 g/10 min or less anda density of between 0.916 and 0.930 g/cm³. The broken lines show whichresins have a δ^(XO) value of between 55° and 70°.

FIG. 8 shows a plot of the shear thinning ratio (η*_(0.1)/η*₁₀) againstthe weight fraction of the first polyethylene copolymer for blends madeaccording to the current invention.

FIG. 9 shows a graph of the melt strength (cN) for blends and blendcomponents according to various embodiments of the present invention.The Figure also shows a plot of the improvement in melt strength (inpercent) for three different blends made according to the invention.

DETAILED DESCRIPTION

Other than in the operating examples or where otherwise indicated, allnumbers or expressions referring to quantities of ingredients, reactionconditions, etc. used in the specification and claims are to beunderstood as modified in all instances by the term “about.”Accordingly, unless indicated to the contrary, the numerical parametersset forth in the following specification and attached claims areapproximations that can vary depending upon the desired properties,which the present invention desires to obtain. At the very least, andnot as an attempt to limit the application of the doctrine ofequivalents to the scope of the claims, each numerical parameter shouldat least be construed in light of the number of reported significantdigits and by applying ordinary rounding techniques.

Notwithstanding that the numerical ranges and parameters setting forththe broad scope of the invention are approximations, the numericalvalues set forth in the specific examples are reported as precisely aspossible. Any numerical values, however, inherently contain certainerrors necessarily resulting from the standard deviation found in theirrespective testing measurements.

Also, it should be understood that any numerical range recited herein isintended to include all sub-ranges subsumed therein. For example, arange of “1 to 10” is intended to include all sub-ranges between andincluding the recited minimum value of 1 and the recited maximum valueof 10; that is, having a minimum value equal to or greater than 1 and amaximum value of equal to or less than 10. Because the disclosednumerical ranges are continuous, they include every value between theminimum and maximum values. Unless expressly indicated otherwise, thevarious numerical ranges specified in this application areapproximations.

All compositional ranges expressed herein are limited in total to and donot exceed 100 percent (volume percent or weight percent) in practice.Where multiple components can be present in a composition, the sum ofthe maximum amounts of each component can exceed 100 percent, with theunderstanding that, and as those skilled in the art readily understand,that the amounts of the components actually used will conform to themaximum of 100 percent.

We recently developed a new polymer composition having goodprocessability and good physical properties. The polymer composition,which can be made with a phosphinimine catalyst, has a density of from0.916 g/cm³ to 0.930 g/cm³, a melt index (I₂) of from about 0.1 to about1.0 g/10 min, a melt flow ratio (I₂₁/I₂) of from about 32 to about 50, amolecular weight distribution (M_(w)/M_(n)) of from 3.6 to 6.0, areverse comonomer distribution profile as determined by GPC-FTIR, amultimodal TREF profile, and a composition distribution breadth indexCDBI₅₀ of from 35 to 70 wt % as determined by TREF. We now report onpolymer blends comprising a similar polymer composition and have foundthat the copolymer composition improves melt strength, shear thinningbehavior and dart impact properties when blended with other linear lowdensity polyethylenes, and brings about good stiffness-toughnessbalance, and good optical properties when blends comprising thecopolymer composition are made into films.

In some embodiments, the present invention provides polymer blends whichhave good processability and melt strength and, when made into film,have a relatively high dart impact strength, as well as good opticalproperties.

In an embodiment of the invention, the polymer blend comprises apolyethylene copolymer having a density of from about 0.916 to about0.936 g/cm³, a melt index (I₂) of from about 0.1 to about 2.0 g/10 min,a melt flow ratio (I₂₁/I₂) of from about 32 to about 50, a molecularweight distribution (M_(w)/M_(n)) of from about 3.6 to about 6.5, areverse comonomer distribution profile as determined by GPC-FTIR, amultimodal TREF profile, and a composition distribution breadth indexCDBI₅₀ of from about 45 to about 75 wt % as determined by TREF; andwhich satisfies at least one of the following relationships:(M _(w) /M _(n))≧72[(I ₂₁ /I ₂)⁻¹+10⁻⁶(M _(n))];δ^(XO) of from 55° to 70°;δ^(XO)≦83.0−1.25(CDBI₅₀)/(M _(w) /M _(n)); orδ^(XO)≦80.7−(CDBI₅₀)/(M _(w) /M _(n)) at a δ^(XO) of from 55° to 70°.

As used herein, the terms “linear low density polyethylene” and “LLDPE”refer to a polyethylene homopolymer or, a copolymer having a density offrom about 0.910 g/cm³ to about 0.945 g/cm³. Unlike high pressure lowdensity polyethylene (HPLDPE), the LLDPE is a linear polymer thatcontains a minimal amount or relatively small amount, or zero amounts oflong chain branching compared to HPLDPE. HPLDPE, in contrast, is oftenreferred to as “branched” because it has a relatively large number oflong chain branches extending from the main polymer backbone.

In the present invention, the term “polyethylene copolymer” is usedinterchangeably with the term “ethylene copolymer”, or “copolymer” andboth connote a polymer comprising polymerized ethylene units and atleast one type of polymerized alpha olefin with ethylene being themajority monomer present.

The comonomers that are useful in general for making polyethylenecopolymers include α-olefins, such as C₃-C₂₀ alpha-olefins, or C₃-C₁₀alpha-olefins, or C₃-C₈ alpha-olefins. The α-olefin comonomer may belinear or branched, and two or more comonomers may be used, if desired.Examples of suitable comonomers include propylene; 1-butene; 1-pentene;1-pentene with one or more methyl, ethyl, or propyl substituents;1-hexene; 1-hexene with one or more methyl, ethyl, or propylsubstituents; 1-heptene; 1-heptene with one or more methyl, ethyl, orpropyl substituents; 1-octene; 1-octene with one or more methyl, ethyl,or propyl substituents; 1-nonene; 1-nonene with one or more methyl,ethyl, or propyl substituents; ethyl, methyl, or dimethyl-substituted1-decene; 1-dodecene; and styrene. Without limitation, the combinationsof ethylene with a comonomer may include: ethylene propylene, ethylenebutene, ethylene 1-pentene; ethylene 4-methyl-1-pentene; ethylene1-hexene; ethylene 1-octene; ethylene decene; ethylene dodecene;ethylene 1-hexene 1-pentene; ethylene 1-hexene 4-methyl-1-pentene;ethylene 1-hexene 1-octene; ethylene 1-hexene decene; ethylene 1-hexenedodecene; ethylene 1-octene 1-pentene; ethylene 1-octene4-methyl-1-pentene; ethylene 1-octene 1-hexene; ethylene 1-octenedecene; ethylene 1-octene dodecene; combinations thereof and likepermutations.

Polyethylene copolymers having more than two types of monomers, such asterpolymers, are also included within the term “copolymer” as usedherein.

In embodiments of the invention, the first and second polyethylenecopolymer blend components will comprise at least about 75 weight % ofethylene units, or at least about 80 wt % of ethylene units, or at leastabout 85 wt % of ethylene units with the balance being an alpha-olefinunit, based on the weight of each blend component.

The term “polymer blend” is herein meant to connote a dry blend of twodifferent polymers, in-reactor blends, including blends arising from theuse of multi or mixed catalyst systems in a single reactor zone, andblends that result from the use of one or more catalysts in one or morereactors under the same or different conditions (e.g., a blend resultingfrom in series reactors each running under different conditions and/orwith different catalysts).

In an embodiment of the invention, the polymer blend will comprise afirst polyethylene copolymer and a second polyethylene copolymer, eachof which are described further below.

The First Polyethylene Copolymer

In some embodiments, the polymer blends of the present inventioncomprises from about 1 to about 99 wt % of a first polyethylenecopolymer which in an embodiment of the invention has a density of fromabout 0.916 g/cm³ to about 0.936 g/cm³, a melt index (I₂) of from about0.1 to about 2.0 g/10 min, a melt flow ratio (I₂₁/I₂) of at least about28, a molecular weight distribution (M_(w)/M_(n)) of from about 3.0 toabout 7.0, a reverse comonomer distribution profile as determined byGPC-FTIR, a multimodal TREF profile, and a composition distributionbreadth index CDBI₅₀ of from about 35 to about 75 wt % as determined byTREF.

In an embodiment of the invention, the first polyethylene copolymersatisfies the following relationship: (M_(w)/M_(n))≧72 [(I₂₁/I₂)⁻¹+10⁻⁶(M_(n))], where Mw/Mn is the molecular weight distribution, Mw is theweight average molecular weight, Mn is the number average molecularweight, I₂ is the melt index in g/10 min, and I₂₁ is the high load meltindex in g/10 min.

In embodiments of the invention, the first polyethylene copolymer has aδ^(XO) of less than about 70° or from about 55° to about 70°, whereδ^(XO) is the crossover phase angle from a Van Gurp-Palmen (VGP) plot asdetermined by dynamic mechanical analysis (DMA).

In an embodiment of the invention, the first polyethylene copolymersatisfies the following relationship: δ^(XO)≦83.0−1.25(CDBI₅₀)/(M_(w)/M_(n)), where δ^(XO) is the crossover phase angle from aVan Gurp-Palmen (VGP) plot as determined by dynamic mechanical analysis(DMA) and CDBI₅₀ is the comonomer distribution breadth index asdetermined by TREF analysis.

In an embodiment of the invention, the first polyethylene copolymersatisfies the following relationship: δ^(XO)≦80.7−(CDBI₅₀)/(M_(w)/M_(n))at a δ^(XO) of from about 55° to about 70°, where δ^(XO) is thecrossover phase angle from a Van Gurp-Palmen (VGP) plot as determined bydynamic mechanical analysis (DMA) and CDBI₅₀ is the comonomerdistribution breadth index as determined by TREF analysis.

In an embodiment of the invention, the first polyethylene copolymersatisfies one or more of the following relationships:

(M_(w)/M_(n))≧72 [(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))], where Mw/Mn is the molecularweight distribution, Mw is the weight average molecular weight, Mn isthe number average molecular weight, I₂ is the melt index in g/10 min,and I₂₁ is the high load melt index in g/10 min;

δ^(XO) of from about 55° to about 70°, where δ^(XO) is the crossoverphase angle from a Van Gurp-Palmen (VGP) plot as determined by dynamicmechanical analysis (DMA);

δ^(XO)≦83.0−1.25 (CDBI₅₀)/(M_(w)/M_(n)), where δ^(XO) is the crossoverphase angle from a Van Gurp-Palmen (VGP) plot as determined by dynamicmechanical analysis (DMA) and CDBI₅₀ is the comonomer distributionbreadth index as determined by TREF analysis; and

δ^(XO)≦80.7−(CDBI₅₀)/(M_(w)/M_(n)) at a δ^(XO) of from about 55° toabout 70°, where δ^(XO) is the crossover phase angle from a VanGurp-Palmen (VGP) plot as determined by dynamic mechanical analysis(DMA) and CDBI₅₀ is the comonomer distribution breadth index asdetermined by TREF analysis.

In embodiments of the invention, the first polyethylene copolymer is acopolymer of ethylene and an alpha olefin selected from 1-butene,1-hexene and 1-octene.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer of ethylene and 1-hexene.

In embodiments of the invention, the first polyethylene copolymercomposition will comprise at least about 75 weight % of ethylene units,or at least about 80 wt % of ethylene units, or at least about 85 wt %of ethylene units with the balance being an alpha-olefin unit, based onthe weight of the ethylene copolymer composition.

In embodiments of the invention, the first polyethylene copolymer willhave a melt index (I₂) of from about 0.01 to about 3.0 g/10 min, or fromabout 0.1 to about 2.5 g/10 min, or from about 0.1 to about 2.0 g/10min, or from about 0.25 to about 2.0 g/10 min, or from about 0.01 toabout 1.0 g/10 min, or from about 0.1 to about 1.0 g/10 min, or lessthan about 1.0 g/10 min, or from about 0.1 to less than about 1.0 g/10min, or from about 0.25 to about 1.0 g/10 min, or from about 0.25 toabout 0.9 g/10 min, or from about 0.25 to about 0.80 g/10 min, or fromabout 0.2 to about 0.9 g/10 min, or from about 0.20 to about 0.85 g/10min, or from about 0.25 to about 0.85 g/10 min. In embodiments of theinvention, the first polyethylene copolymer will have a melt index (I₂)of from greater than about 1.0 to about 2.0 g/10 min, or from greaterthan about 1.0 to about 1.75 g/10 min, or from greater than about 1.0 toabout 1.5 g/10 min.

In an embodiment of the invention, the first polyethylene copolymer hasa melt index (I₂) of less than about 1.0 g/10 min.

In an embodiment of the invention, the first polyethylene copolymer hasmelt index (I₂) of from about 0.25 to about 0.80 g/10 min.

In embodiments of the invention, the first polyethylene copolymer willhave a density of from about 0.916 g/cc to about 0.936 g/cc includingnarrower ranges within this range, such as for example, from about 0.916g/cc to about 0.935 g/cc, or from about 0.916 g/cc to about 0.932 g/cc,or from about 0.916 g/cc to about 0.930 g/cc, or from about 0.917 g/ccto about 0.932 g/cc, or from about 0.917 g/cc to about 0.930 g/cc, orfrom about 0.916 g/cc to about 0.925 g/cc, or from about 0.917 g/cc toabout 0.927 g/cc, or from about 0.917 g/cc to about 0.926 g/cc, or fromabout 0.917 g/cc to about 0.925 g/cc, or from about 0.917 g/cc to about0.923 g/cc, or from about 0.918 g/cc to about 0.932 g/cc, or from about0.918 g/cc to about 0.930 g/cc, or from about 0.918 to about 0.930 g/cc,or from about 0.918 to about 0.928 g/cc, or from about 0.920 to about0.935 (note: “g” stands for gram; “cc” stands for cubic centimeter,cm³).

In an embodiment of the invention, the first polyethylene copolymer willhave a density of from about 0.916 g/cc to about 0.936 g/cc. In anembodiment of the invention, the first polyethylene copolymer will havea density of greater than about 0.916 g/cc to less than about 0.930g/cc. In an embodiment of the invention, the first polyethylenecopolymer will have a density of from about 0.917 g/cc to about 0.927g/cc. In an embodiment of the invention, the first polyethylenecopolymer composition will have a density of from about 0.918 g/cc toabout 0.927 g/cc.

The first polyethylene copolymer may have a unimodal, broad unimodal,bimodal, or multimodal profile in a gel permeation chromatography (GPC)curve generated according to the method of ASTM D6474-99. The term“unimodal” is herein defined to mean there will be one significant peakor maximum evident in the GPC-curve. A unimodal profile includes a broadunimodal profile. By the term “bimodal”, it is meant that there will bea secondary peak or shoulder which represents a higher or lowermolecular weight component (i.e., the molecular weight distribution, canbe said to have two maxima in a molecular weight distribution curve).Alternatively, the term “bimodal” connotes the presence of two maxima ina molecular weight distribution curve generated according to the methodof ASTM D6474-99. The term “multi-modal” denotes the presence of two ormore maxima in a molecular weight distribution curve generated accordingto the method of ASTM D6474-99.

In an embodiment of the invention, the first polyethylene copolymer willhave a unimodal profile in a gel permeation chromatography (GPC) curvegenerated according to the method of ASTM D6474-99.

In embodiments of the invention, the first polyethylene copolymer willexhibit a weight average molecular weight (M_(W)) as determined by gelpermeation chromatography (GPC) of from about 30,000 to about 250,000,including narrower ranges within this range, such as, for example, fromabout 50,000 to about 200,000, or from about 50,000 to about 175,000, orfrom about 75,000 to about 150,000, or from about 80,000 to about130,000.

In embodiments of the invention, the first polyethylene copolymer willexhibit a number average molecular weight (M_(n)) as determined by gelpermeation chromatography (GPC) of from about 5,000 to about 100,000including narrower ranges within this range, such as for example fromabout 7,500 to about 100,000, or from about 7,500 to about 75,000, orfrom about 7,500 to about 50,000, or from about 10,000 to about 100,000,or from about 10,000 to about 75,000, or from about 10,000 to about50,000.

In embodiments of the invention, the first polyethylene copolymer willexhibit a Z-average molecular weight (M_(Z)) as determined by gelpermeation chromatography (GPC) of from about 50,000 to about 1,000,000including narrower ranges within this range, such as for example fromabout 75,000 to about 750,000, or from about 100,000 to about 00,000, orfrom about 100,000 to about 400,000, or from about 125,000 to about375,000, or from about 150,000 to about 350,000, or from about 175,000to about 375,000, or from about 175,000 to about 400,000, or from about200,000 to about 400,000, or from about 225,000 to about 375,000.

In embodiments of the invention, the first polyethylene copolymer willhave a molecular weight distribution (M_(w)/M_(n)) as determined by gelpermeation chromatography (GPC) of from about 3.0 to about 7.0,including narrower ranges within this range, such as, for example, fromabout 3.5 to about 7.0, or from about 3.5 to about 6.5, or from about3.0 to about 6.5, or from about 3.6 to about 6.5, or from about 3.6 toabout 6.0, or from about 3.5 to about 5.5, or from about 3.6 to about5.5, or from about 3.5 to about 5.0, or from about 4.0 to about 6.0, orfrom about 4.0 to about 5.5.

In an embodiment of the invention, the first polyethylene copolymer hasa molecular weight distribution (M_(w)/M_(n)) of from about 4.0 to about5.5.

In embodiments of the invention, the first polyethylene copolymer willhave a Z-average molecular weight distribution (M_(z)/M_(w)) asdetermined by gel permeation chromatography (GPC) of from about 2.0 toabout 5.5, including narrower ranges within this range, such as forexample, from about 2.0 to about 5.0, or from about 2.0 to about 4.5, orfrom about 2.0 to about 4.0, or from about 2.0 to about 2.5, or fromabout 2.0 to about 3.0, or from about 2.0 to about 3.5.

In an embodiment of the invention, the first polyethylene copolymer hasa Z-average molecular weight distribution (M_(z)/M_(w)) of from about2.0 to about 4.0.

In an embodiment of the invention, the first ethylene copolymer willhave a flat comonomer incorporation profile as measured usingGel-Permeation Chromatography with Fourier Transform Infra-Red detection(GPC-FTIR). In an embodiment of the invention, the first ethylenecopolymer will have a negative (i.e., “normal”) comonomer incorporationprofile as measured using GPC-FTIR. In an embodiment of the invention,the first ethylene copolymer will have an inverse (i.e., “reverse”) orpartially inverse comonomer incorporation profile as measured usingGPC-FTIR. If the comonomer incorporation decreases with molecularweight, as measured using GPC-FTIR, the distribution is described as“normal” or “negative”. If the comonomer incorporation is approximatelyconstant with molecular weight, as measured using GPC-FTIR, thecomonomer distribution is described as “flat” or “uniform”. The terms“reverse comonomer distribution” and “partially reverse comonomerdistribution” mean that in the GPC-FTIR data obtained for the copolymer,there is one or more higher molecular weight components having a highercomonomer incorporation than in one or more lower molecular weightsegments. The term “reverse(d) comonomer distribution” is used herein tomean, that across the molecular weight range of the ethylene copolymer,comonomer contents for the various polymer fractions are notsubstantially uniform and the higher molecular weight fractions thereofhave proportionally higher comonomer contents (i.e., if the comonomerincorporation rises with molecular weight, the distribution is describedas “reverse” or “reversed”). Where the comonomer incorporation riseswith increasing molecular weight and then declines slightly or where thecomonomer incorporation initially declines with molecular weight andthen rises at still higher molecular weight, the comonomer distributionis still considered “reverse”, but may also be described as “partiallyreverse”.

In an embodiment of the invention, the first polyethylene copolymer willhave a reversed comonomer incorporation profile as measured usingGPC-FTIR.

In an embodiment of the invention, the first polyethylene copolymer willhave a comonomer incorporation profile as determined by GPC-FTIR whichsatisfies the following condition: SCB/1000 at MW of 200,000−SCB/1000 atMW of 50,000 is a positive number or greater than 1.0; where “−” is aminus sign, SCB/1000 is the comonomer content determined as the numberof short chain branches per thousand carbons and MW is the correspondingmolecular weight (i.e., the absolute molecular weight) on a GPC orGPC-FTIR chromatograph.

In an embodiment of the invention, the first polyethylene copolymer willhave a comonomer incorporation profile as determined by GPC-FTIR whichsatisfies the following condition: SCB/1000 at MW of 200,000−SCB/1000 atMW of 50,000>2.0; where SCB/1000 is the comonomer content determined asthe number of short chain branches per thousand carbons and MW is thecorresponding molecular weight (i.e., the absolute molecular weight) ona GPC or GPC-FTIR chromatograph.

In an embodiment of the invention, the first polyethylene copolymer willhave a comonomer incorporation profile as determined by GPC-FTIR whichsatisfies the following condition: SCB/1000C at MW of 200,000−SCB/1000Cat MW of 50,000>3.0; where SCB/1000C is the comonomer content determinedas the number of short chain branches per thousand carbons and MW is thecorresponding molecular weight (i.e., the absolute molecular weight) ona GPC or GPC-FTIR chromatograph.

In an embodiment of the invention, the first polyethylene copolymer willhave a comonomer incorporation profile as determined by GPC-FTIR whichsatisfies the following condition: SCB/1000C at MW of 200,000−SCB/1000Cat MW of 50,000>4.0; where SCB/1000C is the comonomer content determinedas the number of short chain branches per thousand carbons and MW is thecorresponding molecular weight (i.e., the absolute molecular weight) ona GPC or GPC-FTIR chromatograph.

In an embodiment of the invention, the first polyethylene copolymer willhave a comonomer incorporation profile as determined by GPC-FTIR whichsatisfies the following condition: SCB/1000 at MW of 200,000−SCB/1000 atMW of 50,000>5.0; where SCB/1000 is the comonomer content determined asthe number of short chain branches per thousand carbons and MW is thecorresponding molecular weight (i.e., the absolute molecular weight) ona GPC or GPC-FTIR chromatograph.

In an embodiment of the invention, the first polyethylene copolymer willhave a comonomer incorporation profile as determined by GPC-FTIR whichsatisfies the following condition: SCB/1000 at MW of 200,000−SCB/1000 atMW of 50,000>6.0; where SCB/1000 is the comonomer content determined asthe number of short chain branches per thousand carbons and MW is thecorresponding molecular weight (i.e., the absolute molecular weight) ona GPC or GPC-FTIR chromatograph.

In an embodiment of the invention, the first polyethylene copolymer willhave a comonomer incorporation profile as determined by GPC-FTIR whichsatisfies the following condition: SCB/1000C at MW of 200,000−SCB/1000Cat MW of 50,000 of from about 2.0 to about 8.0 including narrower rangeswithin this range; where SCB/1000C is the comonomer content determinedas the number of short chain branches per thousand carbons and MW is thecorresponding molecular weight (i.e., the absolute molecular weight) ona GPC or GPC-FTIR chromatograph.

In an embodiment of the invention, the first polyethylene copolymer willhave a comonomer incorporation profile as determined by GPC-FTIR whichsatisfies the following condition: SCB/1000C at MW of 200,000−SCB/1000Cat MW of 50,000 of from about 3.0 to about 7.0 including narrower rangeswithin this range; where SCB/1000C is the comonomer content determinedas the number of short chain branches per thousand carbons and MW is thecorresponding molecular weight (i.e., the absolute molecular weight) ona GPC or GPC-FTIR chromatograph.

In embodiments of the invention, the first polyethylene copolymer willhave a melt flow ratio (the MFR=I₂₁/I₂) of from about 28 to about 60, orfrom about 30 to about 60 or from about 32 to about 60. In furtherembodiments of the invention, the copolymer will have an I₂₁/I₂ of atleast about 28, or at least about 30, or from about 30 to about 55, orfrom about 30 to about 50, or from about 30 to about 45, or from about32 to about 50 or from about 35 to about 55, or from about 36 to about50, or from about 36 to about 48, or from about 36 to about 46, or fromabout 35 to about 50, or from greater than about 35 to less than about50, or from greater than about 35 to about 50.

In an embodiment of the invention, the first polyethylene copolymer hasa melt flow ratio (I₂₁/I₂) of from about 32 to about 50. In anembodiment of the invention, the first polyethylene copolymer has a meltflow ratio (I₂₁/I₂) of from about 35 to about 50. In an embodiment ofthe invention, the first polyethylene copolymer has a melt flow ratio(I₂₁/I₂) of from about 36 to about 50.

In embodiments of the invention, the first polyethylene copolymer willhave a composition distribution breadth index CDBI₅₀, as determined bytemperature elution fractionation (TREF) of from about 40% to about 75%by weight, or from about 45% to about 75% by weight, or from about 50%to about 75% by weight, or from about 55% to about 75% by weight, orfrom about 60% to about 75% by weight. In embodiments of the invention,the first polyethylene copolymer will have a CDBI₅₀ of from about 50% toabout 70%, or about 55% to about 70%, or from about 50% to about 69%, orfrom about 55% to about 69%, or from about 55% to about 65%, or fromabout 60% to about 75%, or from about 60% to about 70%, or from about60% to about 69%, or from about 55% to about 67%, or from about 60% toabout 66% (by weight).

In an embodiment of the invention, the first polyethylene copolymer hasa CDBI₅₀ of from about 50 wt % to about 77 wt %. In an embodiment of theinvention, the first polyethylene copolymer has a CDBI₅₀ of from about55 wt % to about 75 wt %. In an embodiment of the invention, the firstpolyethylene copolymer has a CDBI₅₀ of from about 60 wt % to about 73 wt%.

The composition distribution of a polyethylene copolymer may also becharacterized by the T(75)−T(25) value, where the T(25) is thetemperature at which about 25 wt % of the eluted copolymer is obtained,and T(75) is the temperature at which about 75 wt % of the elutedcopolymer is obtained in a TREF experiment as described in the Examplessection.

In an embodiment of the present invention, the first polyethylenecopolymer will have a T(75)−T(25) of from about 5 to about 25° C. asdetermined by TREF. In an embodiment of the present invention, the firstpolyethylene copolymer will have a T(75)−T(25) of from about 7 to about25° C. as determined by TREF. In an embodiment of the present invention,the first polyethylene copolymer will have a T(75)−T(25) of from about10 to about 25° C. as determined by TREF. In an embodiment of thepresent invention, the first polyethylene copolymer will have aT(75)−T(25) of from about 7 to about 22.5° C. as determined by TREF. Inan embodiment of the present invention, the first polyethylene copolymerwill have a T(75)−T(25) of from about 7.0 to about 20° C. as determinedby TREF. In an embodiment of the present invention, the firstpolyethylene copolymer will have a T(75)−T(25) of from about 5 to about17.5° C. as determined by TREF. In an embodiment of the presentinvention, the first polyethylene copolymer will have a T(75)−T(25) offrom about 7 to about 17.5° C. as determined by TREF.

In embodiments of the invention, the first polyethylene copolymer willhave a CY a-parameter (also called the Carreau-Yasuda shear exponent) offrom about 0.01 to about 0.4, or from about 0.05 to about 0.4, or fromabout 0.05 to about 0.3, or from about 0.01 to about 0.3, or from about0.01 to about 0.25, or from about 0.05 to about 0.30, or from about 0.05to about 0.25.

In embodiments of the invention, the first polyethylene copolymer willhave a normalized shear thinning index, SHI @0.1 rad/s (i.e., theη*_(0.1)/η₀) of from about 0.001 to about 0.90, or from about 0.001 toabout 0.8, or from about 0.001 to about 0.5, or less than about 0.9, orless than about 0.8, or less than about 0.5.

In an embodiment of the invention, the first polyethylene copolymer willhave a TREF profile, as measured by temperature rising elutionfractionation, which is multimodal, comprising at least two elutionintensity maxima or peaks.

In an embodiment of the invention, the first polyethylene copolymer willhave an amount of copolymer eluting at a temperature at or below about40° C., of less than about 5 wt % as determined by temperature risingelution fractionation (TREF).

In an embodiment of the invention, the first polyethylene copolymer willhave an amount of copolymer eluting at a temperature of from about 90°C. to about 105° C., of from about 5 to about 30 wt % as determined bytemperature rising elution fractionation (TREF). In an embodiment of theinvention, from about 5 to about 25 wt % of the first polyethylenecopolymer will be represented within a temperature range of from about90° C. to about 105° C. in a TREF profile. In an embodiment of theinvention, from about 7.5 to about 25 wt % of the first polyethylenecopolymer will be represented within a temperature range of from about90° C. to about 105° C. in a TREF profile. In an embodiment of theinvention, from about 10 to about 25 wt % of the first polyethylenecopolymer will be represented within a temperature range of from about90° C. to about 105° C. in a TREF profile.

In another embodiment of the invention, from about 5 to about 22.5 wt %of the first polyethylene copolymer will be represented at a temperaturerange of from about 90° C. to about 105° C. in a TREF profile. Inanother embodiment of the invention, from about 5 to about 20.0 wt % ofthe first polyethylene copolymer will be represented at a temperaturerange of from about 90° C. to about 105° C. in a TREF profile.

In embodiments of the invention, less than about 1 wt %, or less thanabout 0.5 wt %, or less than about 0.05 wt %, or about 0 wt % of thefirst polyethylene copolymer will elute at a temperature of above about100° C. in a TREF analysis.

In an embodiment of the invention, the first polyethylene copolymer willhave a TREF profile, as measured by temperature rising elutionfractionation, comprising: i) a multimodal TREF profile comprising atleast two elution intensity maxima (or peaks); ii) less than about 5 wt% of the copolymer represented at a temperature at or below about 40°C.; and iii) from about 5 to about 25 wt % of the copolymer representedat a temperature of from about 90° C. to about 105° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile comprising at least two elution intensitymaxima (or peaks).

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by at least two intensity maxima (orpeaks) occurring at elution temperatures T(low), and T(high), whereT(low) is from about 60° C. to about 87° C., and T(high) is from about88° C. to about 100° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by at least two intensity maxima (orpeaks) occurring at elution temperatures T(low), and T(high), whereT(low) is from about 62° C. to about 87° C., and T(high) is from about89° C. to about 100° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by at least two intensity maxima (orpeaks) occurring at elution temperatures T(low), and T(high), whereT(low) is from about 65° C. to about 85° C., and T(high) is from about90° C. to about 100° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by at least two intensity maxima (orpeaks) occurring at elution temperatures T(low), and T(high), whereT(low) is from about 65° C. to about 85° C., and T(high) is from about90° C. to about 98° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by at least two intensity maxima (orpeaks) occurring at elution temperatures T(low), and T(high), whereT(low) is from about 70° C. to about 85° C., and T(high) is from about90° C. to about 98° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by at least two intensity maxima (orpeaks) occurring at elution temperatures T(low), and T(high), whereT(low) is from about 70° C. to about 80° C., and T(high) is from about90° C. to about 98° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by at least two intensity maxima (orpeaks) occurring at elution temperatures T(low), and T(high), whereT(low) is from about 70° C. to about 80° C., and T(high) is from about90° C. to about 95° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by at least two elution intensitymaxima (or peaks) occurring at elution temperatures T(low), and T(high),where (high)−T(low) is from about 7.5° C. to about 35° C., or from about10.0° C. to about 30° C., or from about 12.5° C. to about 30° C., orfrom about 7.0° C. to about 27° C., or from about 7° C. to about 25° C.,or from about 10° C. to about 27° C., or from about 10° C. to about 25°C., or from about 10° C. to about 22.5° C., or from about 12.5° C. toabout 22.5° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by at least two intensity maxima (orpeaks) occurring at elution temperatures T(low), and T(high), whereT(low) is from about 65° C. to 85° C., and T(high) is from about 90° C.to about 98° C., where (high)−T(low) is from about 7.5° C. to about 35°C., or from about 10.0° C. to about 30° C., or from about 12.5° C. toabout 30° C., or from about 7.0° C. to about 27° C., or from about 7° C.to about 25° C., or from about 10° C. to about 27° C., or from about 10°C. to about 25° C., or from about 10° C. to about 22.5° C., or fromabout 12.5° C. to about 22.5° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile comprising at least three elution intensitymaxima (or peaks).

In an embodiment of the invention, the first polyethylene copolymer hasa trimodal TREF profile comprising three elution intensity maxima (orpeaks).

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where the intensity of the peaks at T(low) andT(high) is greater than the intensity of the peak at T(med).

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(low) is from about 60° C. to about 87° C.,T(high) is from about 88° C. to about 100° C., and T(med) is higher thanT(low), but lower than T(high).

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(low) is from about 62° C. to about 87° C.,T(high) is from about 89° C. to about 100° C., and T(med) is higher thanT(Iow), but lower than T(high).

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(low) is from about 65° C. to about 85° C.,T(high) is from about 90° C. to about 100° C., and T(med) is higher thanT(low), but lower than T(high).

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(low) is from about 65° C. to about 85° C.,T(high) is from about 90° C. to about 98° C., and T(med) is higher thanT(low), but lower than T(high).

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(Iow) is from about 65° C. to about 80° C.,T(high) is from about 90° C. to about 98° C., and T(med) is higher thanT(low), but lower than T(high).

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(Iow), T(medium or “med” forshort) and T(high), where T(low) is from about 65° C. to about 87° C.,T(high) is from about 88° C. to about 100° C., and T(med) is higher thanT(low), but lower than T(high), where (high)−T(low) is from about 7.5°C. to about 35° C., or from about 10.0° C. to about 30° C., or fromabout 12.5° C. to about 30° C., or from about 7.0° C. to about 27° C.,or from about 7° C. to about 25° C., or from about 10° C. to about 27°C., or from about 10° C. to about 25° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(Iow) is from about 62° C. to about 82° C.,T(med) is from about 76° C. to about 89° C. but is higher than T(low),and T(high) is from about 90° C. to about 100° C. In an embodiment ofthe invention, the first polyethylene copolymer has a multimodal TREFprofile defined by three elution intensity maxima (or peaks) occurringat elution temperatures T(low), T(medium or “med” for short) andT(high), where T(low) is from about 65° C. to about 80° C., T(med) isfrom about 75° C. to about 90° C. but is higher than T(low), and T(high)is from about 90° C. to about 100° C. but is higher than T(med). In anembodiment of the invention, the first polyethylene copolymer has amultimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(low) is from about 67° C. to about 78° C.,T(med) is from about 79° C. to about 89° C., and T(high) is from about90° C. to about 100° C. In an embodiment of the invention, the firstpolyethylene copolymer has a multimodal TREF profile defined by threeelution intensity maxima (or peaks) occurring at elution temperaturesT(low), T(medium or “med” for short) and T(high), where T(low) is fromabout 67° C. to about 78° C., T(med) is from about 80° C. to about 87°C., and T(high) is from about 88° C. to about 98° C.

In embodiments of the invention, the first polyethylene copolymer has amultimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(med)−T(low) is from about 3° C. to about 25°C., or from about 5° C. to about 20° C.; or from about 5° C. to about15° C., or from about 7° C. to about 15° C.

In embodiments of the invention, the first polyethylene copolymer has amultimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(high)−T(med) is from about 3° C. to about20° C., or from about 3° C. to about 17° C., or from about 3° C. toabout 15° C., or from about 5° C. to about 20° C., or from about 5° C.to about 17° C., or from about 5° C. to about 15° C., or from about 7°C. to about 17° C., or from about 7° C. to about 15° C. or from about10° C. to about 17° C., or from about 10° C. to about 15° C.

In embodiments of the invention, the first polyethylene copolymer has amultimodal TREF profile defined by three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where T(high)−T(low) is from about 15° C. to about35° C., or from about 15° C. to about 30° C., or from 1 about 7° C. toabout 30° C., or from about 15° C. to about 27° C., or from about 17° C.to about 27° C., or from about 20° C. to about 30° C. or from about 20°C. to about 27° C., or from about 15° C. to about 25° C. or from about15° C. to about 22.5° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile comprising three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where the intensity of the peaks at T(low) andT(high) are greater than the intensity of the peak at T(med); and whereT(med)−T(low) is from about 3° C. to about 25° C.; where T(high)−T(med)is from about 5° C. to about 15° C.; and where T(high)−T(low) is fromabout 15° C. to about 35° C.

In an embodiment of the invention, the first polyethylene copolymer hasa multimodal TREF profile comprising three elution intensity maxima (orpeaks) occurring at elution temperatures T(low), T(medium or “med” forshort) and T(high), where the intensity of the peaks at T(low) andT(high) are greater than the intensity of the peak at T(med); and whereT(med)−T(low) is from about 3° C. to about 15° C.; where T(high)−T(med)is from about 5° C. to about 15° C.; and where T(high)−T(low) is fromabout 15° C. to about 30° C.

In an embodiment of the invention, the first polyethylene copolymer hastwo melting peaks as measured by differential scanning calorimetry(DSC).

In embodiments of the invention, the first polyethylene copolymer willhave a hexane extractables level of ≦ about 3.0 wt %, or ≦ about 2.0 wt%, or ≦ about 1.5 wt % or ≦ about 1.0 wt %. In an embodiment of theinvention, the first polyethylene copolymer has a hexane extractableslevel of from about 0.2 to about 3.0 wt %, or from about 0.2 to about2.5 wt %, or from about 0.2 to about 2.0 wt %, or from about 0.2 toabout 1.0 wt %.

The Second Polyethylene Copolymer

The polymer blend may comprise from about 99 to about 1 wt % of secondpolyethylene copolymer. The second polyethylene copolymer is a linearlow density polyethylene (LLDPE). The second polyethylene copolymer maybe a different polymer than the first polyethylene copolymer. The secondpolyethylene copolymer can be distinguished from the first polyethylenecopolymer by differing in at least one property or characteristic. Byway of non-limiting example, the second polyethylene copolymer can bedistinguished from the first polyethylene copolymer by not satisfyingthe following relationship: (M_(w)/M_(n))≧72 [(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))].Alternatively, and also by way of non-limiting example, the secondpolyethylene copolymer can be distinguished from the first polyethylenecopolymer by having a lower melt flow ratio (I₂₁/I₂) than the firstpolyethylene copolymer.

In an embodiment of the invention, the second polyethylene copolymer hasa density of from about 0.910 g/cm³ to about 0.940 g/cm³. In anembodiments of the invention, the second polyethylene copolymer willhave a density ranging from a low of about 0.910 g/cm³, or about 0.912g/cm³, or about 0.915 g/cm³, or about 0.916 g/cm³, or about 0.917 g/cm³to a high of about 0.927 g/cm³, or about 0.930 g/cm³, or about 0.935g/cm³, or about 0.940 g/cm³. In an embodiments of the invention, thesecond polyethylene copolymer will have a density of from about 0.912g/cm³ to about 0.940 g/cm³, or from about 0.915 g/cm³ to about 0.935g/cm³, or from about 0.915 to about 0.930 g/cm³, or from about 0.916 toabout 0.930 g/cm³, or from about 0.915 to about 0.925 g/cm³, or fromabout 0.916 to about 0.924 g/cm³, or from about 0.917 to about 0.923g/cm³, or from about 0.918 to about 0.922 g/cm³.

In an embodiment of the invention, the second polyethylene copolymerwill have a molecular weight distribution (Mw/Mn) of from about 1.5 toabout 6.0. In embodiments of the invention, the second polyethylenecopolymer will have a molecular weight distribution (Mw/Mn) ranging froma low of about 1.5, or about 1.7, or about 2.0, or about 2.5, or about3.0, or about 3.5, or about 3.7, or about 4.0 to a high of about 5, orabout 5.25, or about 5.5, or about 6.0. In embodiments of the invention,the second polyethylene copolymer will have a molecular weightdistribution (Mw/Mn) of from about 1.7 to about 5.0, or from about 1.5to about 4.0, or from about 1.8 to about 3.5, or from about 2.0 to about3.0. Alternatively, in embodiments of the invention, the secondpolyethylene copolymer will have a molecular weight distribution (Mw/Mn)of from about 3.6 to about 5.4, or from about 3.8 to about 5.1, or fromabout 3.9 to about 4.9.

In an embodiment of the invention, the second polyethylene copolymerwill have a melt index (I₂) of from about 0.1 g/10 min to about 20 g/10min. In embodiments of the invention, the second polyethylene copolymerwill have a melt index (I₂) ranging from about 0.75 g/10 min to about 15g/10 min, or from about 0.85 g/10 min to about 10 g/10 min, or fromabout 0.9 g/10 min to about 8 g/10 min. In embodiments of the invention,the second polyethylene copolymer will have a melt index (I₂) rangingfrom a low of about 0.20 g/10 min, or about 0.25 g/10 min, or about 0.5g/10 min, or about 0.75 g/10 min, or about 1 g/10 min, or about 2 g/10min to a high of about 3 g/10 min, or about 4 g/10 min, or about 5 g/10min.

In embodiments of the invention the second polyethylene copolymer willhave a melt index (I₂) of from about 0.75 g/10 min to about 6 g/10 min,or from about 1 g/10 min to about 8 g/10 min, or from about 0.8 g/10 minto about 6 g/10 min, or from about 1 g/10 min to about 4.5 g/10 min, orfrom about 0.20 g/10 min to about 5.0 g/10 min, or from about 0.30 g/10min to about 5.0 g/10 min, or from about 0.40 g/10 min to about 5.0 g/10min, or from about 0.50 g/10 min to about 5.0 g/10 min.

In embodiments of the invention, the second polyethylene copolymer willhave a melt flow ratio (I₂₁/I₂) of less than about 36, or less thanabout 35, or less than about 32, or less than about 30. In embodimentsof the invention, the second polyethylene copolymer will have a meltflow ratio (I₂₁/I₂) of from about 10 to about 36, or from about 10 toabout 35, or from about 10 to about 32, or from about 10 to about 30, orfrom about 12 to about 35 or from about 12 to about 32, or from about 12to about 30, or from about 14 to about 27, or from about 14 to about 25,or from about 14 to about 22, or from about 15 to about 20.

In an embodiment of the invention, the second polyethylene copolymerwill have a CBDI₅₀ of ≧ about 50 weight percent or a CBDI₅₀ of ≦ about50 weight percent as determined by TREF analysis.

In embodiments of the invention, the second polyethylene copolymer willhave a composition distribution breadth index CDBI₅₀, as determined bytemperature elution fractionation (TREF), of from about 25% to about 95%by weight, or from about 35 to about 90% by weight, or from about 40% toabout 85% by weight, or from about 40% to about 80% by weight.

Catalysts and Process

The first and second polyethylene copolymers can be made using anyappropriate catalyst, including for example so called single sitecatalysts, or a traditional Ziegler-Natta catalysts or chromium basedcatalysts. Processes such as solution phase polymerization, gas phasepolymerization or slurry phase polymerization can be employed to makethe first and second polyethylene copolymers.

Illustrative Ziegler-Natta catalyst compounds are disclosed in ZieglerCatalysts 363-386 (G. Fink, R. Mulhaupt and H. H. Brintzinger, eds.,Springer-Verlag 1995); European Patent Nos. EP 103120; EP 102503; EP231102; EP 703246; U.S. Pat. Nos. 4,115,639; 4,077,904; 4,302,565;4,302,566; 4,482,687; 4,564,605; 4,721,763; 4,879,359; 4,960,741;5,518,973; 5,525,678; 5,288,933; 5,290,745; 5,093,415; and 6,562,905;and U.S. Patent Application Publication No. 2008/0194780. Examples ofsuch catalysts include those comprising Group 4, 5 or 6 transition metaloxides, alkoxides and halides, or oxides, alkoxides and halide compoundsof titanium, zirconium or vanadium; optionally in combination with amagnesium compound, internal and/or external electron donors (alcohols,ethers, siloxanes, etc.), aluminum or boron alkyl and alkyl halides, andinorganic oxide supports.

Illustrative examples of chromium based polymerization catalysts includePhillips polymerization catalysts, chromium oxide catalysts, silylchromate catalysts, and chromocene catalysts, examples of which aredescribed in for example U.S. Pat. Nos. 4,077,904, 4,115,639, 2,825,721,3,023,203, 3,622,251, 4,011,382, 3,704,287, 4,100,105 and US Pat. App.Pub. No. US20120302707 and the references therein.

Single site catalysts include, for example, phosphinimine catalysts(which have at least one phosphinimine ligand), metallocene catalysts(which have two cyclopentadienyl type ligands), and constrained geometrycatalysts (which have an amido type ligand and a cyclopentadienyl typeligand).

Some non-limiting examples of phosphinimine catalysts can be found inU.S. Pat. Nos. 6,342,463; 6,235,672; 6,372,864; 6,984,695; 6,063,879;6,777,509 and 6,277,931 all of which are incorporated by referenceherein.

Some non-limiting examples of metallocene catalysts, which may or maynot be useful, can be found in U.S. Pat. Nos. 4,808,561; 4,701,432;4,937,301; 5,324,800; 5,633,394; 4,935,397; 6,002,033 and 6,489,413,which are incorporated herein by reference.

Some non-limiting examples of constrained geometry catalysts, which mayor may not be useful, can be found in U.S. Pat. Nos. 5,057,475;5,096,867; 5,064,802; 5,132,380; 5,703,187 and 6,034,021, all of whichare incorporated by reference herein in their entirety.

In some embodiments, an activator may be used with the catalystcompound. As used herein, the term “activator” refers to any compound orcombination of compounds, supported or unsupported, which can activate acatalyst compound or component, such as by creating a cationic speciesof the catalyst component. Illustrative activators include, but are notlimited to, aluminoxane (e.g., methylaluminoxane “MAO”), modifiedaluminoxane (e.g., modified methylaluminoxane “MMAO” and/ortetraisobutyldialuminoxane “TIBAO”), alkylaluminum compounds, ionizingactivators (neutral or ionic) such as tri(n-butyl)ammoniumtetrakis(pentafluorophenyl)boron and combinations thereof.

The catalyst compositions can include a support material or carrier. Asused herein, the terms “support” and “carrier” are used interchangeablyand are any support material, including a porous support material, forexample, talc, inorganic oxides, and inorganic chlorides. The catalystcomponent(s) and/or activator(s) can be deposited on, contacted with,vaporized with, bonded to, or incorporated within, adsorbed or absorbedin, or on, one or more supports or carriers. Other support materials caninclude resinous support materials such as polystyrene, functionalizedor crosslinked organic supports, such as polystyrene divinyl benzenepolyolefins or polymeric compounds, zeolites, clays, or any otherorganic or inorganic support material and the like, or mixtures thereof.Suitable catalyst supports are discussed and described in, for example,Hlatky, Chem. Rev. (2000), 100, 1347 1376 and Fink et al, Chem. Rev.(2000), 100, 1377 1390, U.S. Pat. Nos. 4,701,432; 4,808,561; 4,912,075;4,925,821; 4,937,217; 5,008,228; 5,238,892; 5,240,894; 5,332,706;5,346,925; 5,422,325; 5,466,649; 5,466,766; 5,468,702; 5,529,965;5,554,704; 5,629,253; 5,639,835; 5,625,015; 5,643,847; 5,665,665;5,698,487; 5,714,424; 5,723,400; 5,723,402; 5,731,261; 5,759,940;5,767,032; 5,770,664; and 5,972,510; and PCT Publication Nos. WO95/32995; WO 95/14044; WO 96/06187; WO 97/02297; WO 99/47598; WO99/48605; and WO 99/50311.

In an embodiment of the invention, the first polyethylene copolymer ismade with a polymerization catalyst system comprising a phosphiniminecatalyst.

In an embodiment of the invention, the first polyethylene copolymer ismade using a catalyst system comprising a phosphinimine catalyst, asupport, and a catalyst activator.

In an embodiment of the invention, the first polyethylene copolymer ismade in the gas phase using a catalyst system comprising a phosphiniminecatalyst, a support, and a catalyst activator.

In an embodiment of the invention, the first polyethylene copolymer ismade in a single gas phase reactor using a catalyst system comprising aphosphinimine catalyst, a support, and a catalyst activator.

The phosphinimine catalyst is based on metals from group 4, whichincludes titanium, hafnium and zirconium. In one embodiment, thephosphinimine catalysts are group 4 metal complexes in their highestoxidation state.

The phosphinimine catalysts described herein, usually require activationby one or more cocatalytic or activator species in order to providepolymer from olefins.

A phosphinimine catalyst is a compound (typically an organometalliccompound) based on a group 3, 4 or 5 metal and which is characterized ashaving at least one phosphinimine ligand. Any compounds/complexes havinga phosphinimine ligand and which display catalytic activity for ethylene(co)polymerization may be called “phosphinimine catalysts”.

In an embodiment of the invention, a phosphinimine catalyst is definedby the formula: (L)_(n)(Pl)_(m)MX_(p) where M is a transition metalselected from Ti, Hf, Zr; Pl is a phosphinimine ligand; L is acyclopentadienyl type ligand; X is an activatable ligand; m is 1 or 2; nis 0 or 1; and p is determined by the valency of the metal M. In oneembodiment m is 1, n is 1 and p is 2.

In an embodiment of the invention, a phosphinimine catalyst is definedby the formula: (L)(Pl)MX₂ where M is a transition metal selected fromTi, Hf, Zr; Pl is a phosphinimine ligand; L is a cyclopentadienyl typeligand; and X is an activatable ligand.

In an embodiment of the invention, the phosphinimine catalyst will havea phosphinimine ligand which is not bridged to, or does not make abridge with another ligand within the metal coordination sphere of thephosphinimine catalyst, such as for example a cyclopentadienyl typeligand.

In an embodiment of the invention, the phosphinimine catalyst will havea cyclopentadienyl type ligand which is not bridged to, or does not makea bridge with another ligand within the metal coordination sphere of thephosphinimine catalyst, such as for example a phosphinimine ligand.

The phosphinimine ligand is defined by the formula: R¹ ₃P═N— whereineach R¹ is independently selected from a hydrogen atom; a halogen atom;a C₁₋₃₀ hydrocarbyl radical which is unsubstituted or furthersubstituted by one or more halogen atom; a C₁₋₂₀ alkyl radical; a C₁₋₈alkoxy radical; a C₆₋₁₀ aryl or aryloxy radical; an amido radical; asilyl radical; and a germanyl radical; P is phosphorus and N is nitrogen(and bonds to the metal M).

In an embodiment of the invention, the phosphinimine ligand is chosen sothat each R¹ is a hydrocarbyl radical. In a particular embodiment of theinvention, the phosphinimine ligand is tri-(tertiarybutyl)phosphinimine(i.e., where each R¹ is a tertiary butyl group).

As used herein, the term “cyclopentadienyl-type” ligand is meant toinclude ligands which contain at least one five carbon ring which isbonded to the metal via eta-5 (or in some cases eta-3) bonding. Thus,the term “cyclopentadienyl-type” includes, for example, unsubstitutedcyclopentadienyl, singly or multiply substituted cyclopentadienyl,unsubstituted indenyl, singly or multiply substituted indenyl,unsubstituted fluorenyl and singly or multiply substituted fluorenyl.Hydrogenated versions of indenyl and fluorenyl ligands are alsocontemplated for use in the current invention, so long as the fivecarbon ring which bonds to the metal via eta-5 (or in some cases eta-3)bonding remains intact. Substituents for a cyclopentadienyl ligand, anindenyl ligand (or hydrogenated version thereof) and a fluorenyl ligand(or hydrogenated version thereof) can be selected from a C₁₋₃₀hydrocarbyl radical (which hydrocarbyl radical may be unsubstituted orfurther substituted by for example a halide and/or a hydrocarbyl group;for example a suitable substituted C₁₋₃₀ hydrocarbyl radical is apentafluorobenzyl group such as —CH₂C₆F₅); a halogen atom; a C₁₋₈ alkoxyradical; a C₆₋₁₀ aryl or aryloxy radical (each of which may be furthersubstituted by for example a halide and/or a hydrocarbyl group); anamido radical which is unsubstituted or substituted by up to two C₁₋₈alkyl radicals; a phosphido radical which is unsubstituted orsubstituted by up to two C₁₋₈ alkyl radicals; a silyl radical of theformula —Si(R′)₃ wherein each R′ is independently selected fromhydrogen, a C₁₋₈ alkyl or alkoxy radical, C₆₋₁₀ aryl and C₆₋₁₀ aryloxyradicals; and a germanyl radical of the formula —Ge(R′)₃ wherein R′ isas defined directly above.

The term “perfluorinated aryl group” means that each hydrogen atomattached to a carbon atom in an aryl group has been replaced with afluorine atom as is well understood in the art (e.g., a perfluorinatedphenyl group or substituent has the formula —C₆F₅).

In an embodiment of the invention, the phosphinimine catalyst will havea single or multiply substituted indenyl ligand and a phosphinimineligand which is substituted by three tertiary butyl substituents.

An indenyl ligand (or “Ind” for short) as defined herein will haveframework carbon atoms with the numbering scheme provided below, so thelocation of a substituent can be readily identified.

In an embodiment of the invention, the phosphinimine catalyst will havea singly substituted indenyl ligand and a phosphinimine ligand which issubstituted by three tertiary butyl substituents.

In an embodiment of the invention, the phosphinimine catalyst will havea singly or multiply substituted indenyl ligand where the substituent isselected from a substituted or unsubstituted alkyl group, a substitutedor an unsubstituted aryl group, and a substituted or unsubstitutedbenzyl (i.e., C₆H₅CH₂—) group. Suitable substituents for the alkyl, arylor benzyl group may be selected from alkyl groups, aryl groups, alkoxygroups, aryloxy groups, alkylaryl groups (e.g., a benzyl group),arylalkyl groups and halide groups.

In an embodiment of the invention, the phosphinimine catalyst will havea singly substituted indenyl ligand, R²-Indenyl, where the R²substituent is a substituted or unsubstituted alkyl group, a substitutedor an unsubstituted aryl group, or a substituted or unsubstituted benzylgroup. Suitable substituents for an R² alkyl, R² aryl or R² benzyl groupmay be selected from alkyl groups, aryl groups, alkoxy groups, aryloxygroups, alkylaryl groups (e.g., a benzyl group), arylalkyl groups andhalide groups.

In an embodiment of the invention, the phosphinimine catalyst will havean indenyl ligand having at least a 1-position substituent (1-R²) wherethe substituent R² is a substituted or unsubstituted alkyl group, asubstituted or an unsubstituted aryl group, or a substituted orunsubstituted benzyl group. Suitable substituents for an R² alkyl, R²aryl or R² benzyl group may be selected from alkyl groups, aryl groups,alkoxy groups, aryloxy groups, alkylaryl groups (e.g., a benzyl group),arylalkyl groups and halide groups.

In an embodiment of the invention, the phosphinimine catalyst will havea singly substituted indenyl ligand, 1-R²-Indenyl where the substituentR² is in the 1-position of the indenyl ligand and is a substituted orunsubstituted alkyl group, a substituted or unsubstituted aryl group, ora substituted or an unsubstituted benzyl group. Suitable substituentsfor an R² alkyl, R² aryl or R² benzyl group may be selected from alkylgroups, aryl groups, alkoxy groups, aryloxy groups, alkylaryl groups(e.g., a benzyl group), arylalkyl groups and halide groups.

In an embodiment of the invention, the phosphinimine catalyst will havea singly substituted indenyl ligand, 1-R²-Indenyl, where the substituentR² is a (partially/fully) halide substituted alkyl group, a(partially/fully) halide substituted benzyl group, or a(partially/fully) halide substituted aryl group.

In an embodiment of the invention, the phosphinimine catalyst will havea singly substituted indenyl ligand, 1-R²-Indenyl, where the substituentR² is a (partially/fully) halide substituted benzyl group.

When present on an indenyl ligand, a benzyl group can be partially orfully substituted by halide atoms, for example, fluoride atoms. The arylgroup of the benzyl group may be a perfluorinated aryl group, a 2,6(i.e., ortho) fluoro substituted phenyl group, 2,4,6 (i.e., ortho/para)fluoro substituted phenyl group or a 2,3,5,6 (i.e., ortho/meta) fluorosubstituted phenyl group respectively. The benzyl group is, in anembodiment of the invention, located at the 1 position of the indenylligand.

In an embodiment of the invention, the phosphinimine catalyst will havea singly substituted indenyl ligand, 1-R²-Indenyl, where the substituentR² is a pentafluorobenzyl (C₆F₅CH₂—) group.

In an embodiment of the invention, the phosphinimine catalyst has theformula: (1-R²—(Ind))M(N═P(t-Bu)₃)X₂ where R² is a substituted orunsubstituted alkyl group, a substituted or an unsubstituted aryl group,or a substituted or unsubstituted benzyl group, wherein substituents forthe alkyl, aryl or benzyl group are selected from alkyl, aryl, alkoxy,aryloxy, alkylaryl, arylalkyl and halide substituents; M is Ti, Zr orHf; and X is an activatable ligand.

In an embodiment of the invention, the phosphinimine catalyst has theformula: (1-R²—(Ind))M(N═P(t-Bu)₃)X₂ where R² is an alkyl group, an arylgroup or a benzyl group and wherein each of the alkyl group, the arylgroup, and the benzyl group may be unsubstituted or substituted by atleast one fluoride atom; M is Ti, Zr or Hf; and X is an activatableligand.

In an embodiment of the invention, the phosphinimine catalyst has theformula: (1-R²—(Ind))M(N═P(t-Bu)₃)X₂ where R² is an alkyl group, an arylgroup or a benzyl group and wherein each of the alkyl group, the arylgroup, and the benzyl group may be unsubstituted or substituted by atleast one halide atom; M is Ti, Zr or Hf; and X is an activatableligand.

In an embodiment of the invention, the phosphinimine catalyst has theformula: (1-R²—(Ind))Ti(N═P(t-Bu)₃)X₂ where R² is an alkyl group, anaryl group or a benzyl group and wherein each of the alkyl group, thearyl group, and the benzyl group may be unsubstituted or substituted byat least one fluoride atom; and X is an activatable ligand.

In an embodiment of the invention, the phosphinimine catalyst has theformula: (1-C₆F₅CH₂-Ind)M(N═P(t-Bu)₃)X₂, where M is Ti, Zr or Hf; and Xis an activatable ligand.

In an embodiment of the invention, the phosphinimine catalyst has theformula: (1-C₆F₅CH₂-Ind)Ti(N═P(t-Bu)₃)X₂, where X is an activatableligand.

In the current invention, the term “activatable”, means that the ligandX may be cleaved from the metal center M via a protonolysis reaction orabstracted from the metal center M by suitable acidic or electrophiliccatalyst activator compounds (also known as “co-catalyst” compounds)respectively, examples of which are described below. The activatableligand X may also be transformed into another ligand which is cleaved orabstracted from the metal center M (e.g., a halide may be converted toan alkyl group). Without wishing to be bound by any single theory,protonolysis or abstraction reactions generate an active “cationic”metal center which can polymerize olefins.

In embodiments of the present invention, the activatable ligand, X isindependently selected from a hydrogen atom; a halogen atom, a C₁₋₁₀hydrocarbyl radical; a C₁₋₁₀ alkoxy radical; and a C₆₋₁₀ aryl or C₆₋₁₀aryloxy radical, (where each of the hydrocarbyl, alkoxy, aryl, or aryloxide radicals may be un-substituted or further substituted by one ormore halogen or other group such as for example, a C₁₋₈ alkyl; a C₁₋₈alkoxy, a C₆₋₁₀ aryl or C₆₋₁₀ aryloxy); an amido and a phosphidoradical, but where X is not a cyclopentadienyl. Two X ligands may alsobe joined to one another and form for example, a substituted orunsubstituted diene ligand (e.g., 1,3-butadiene); or a delocalizedheteroatom containing group such as an acetate or acetamidinate group.In one embodiment of the invention, each X is independently selectedfrom a halide atom, a C₁₋₄ alkyl radical and a benzyl radical.

Particularly suitable activatable ligands are monoanionic such as ahalide (e.g. chloride) or a hydrocarbyl (e.g., methyl, benzyl).

The catalyst activator used to activate the phosphinimine polymerizationcatalyst can be any suitable activator including one or more activatorsselected from alkylaluminoxanes and ionic activators, optionallytogether with an alkylating agent.

Without wishing to be bound by theory, alkylaluminoxanes are thought tobe complex aluminum compounds of the formula:

R³ ₂Al¹O(R³Al¹O)_(m)Al¹R³ ₂, wherein each R³ is independently selectedfrom C₁₋₂₀ hydrocarbyl radicals and m is from 3 to 50. Optionally, ahindered phenol can be added to the alkylaluminoxane to provide a molarratio of Al¹:hindered phenol of from about 2:1 to about 5:1 when thehindered phenol is present.

In an embodiment of the invention, R³ of the alkylaluminoxane, is amethyl radical and m is from about 10 to about 40.

In an embodiment of the invention, the cocatalyst is methylaluminoxane(MAO).

In an embodiment of the invention, the cocatalyst is modifiedmethylaluminoxane (MMAO).

The alkylaluminoxanes are typically used in substantial molar excesscompared to the amount of group 4 transition metal in the phosphiniminecatalyst. The Al¹:group 4 transition metal molar ratios may be fromabout 10:1 to about 10,000:1, or from about 30:1 to about 500:1.

It is well known in the art, that the alkylaluminoxane can serve dualroles as both an alkylator and an activator. Hence, an alkylaluminoxaneactivator is often used in combination with activatable ligands such ashalogens.

Alternatively, the catalyst activator may be a combination of analkylating agent (which may also serve as a scavenger) with an activatorcapable of ionizing the group 4 of the phosphinimine catalyst metalcatalyst (i.e., an ionic activator). In this context, the activator canbe chosen from one or more alkylaluminoxane and/or an ionic activator,since an alkylaluminoxane may serve as both an activator and analkylating agent.

When present, the alkylating agent may be selected from (R⁴)_(p)MgX²_(2-p) wherein X² is a halide and each R⁴ is independently selected fromC₁₋₁₀ alkyl radicals and p is 1 or 2; R⁴Li wherein in R⁴ is as definedabove, (R⁴)_(q)ZnX² _(2-q) wherein R⁴ is as defined above, X² is halogenand q is 1 or 2; (R⁴)_(s)Al²X² _(3-s) wherein R⁴ is as defined above, X²is halogen and s is an integer from 1 to 3. In one embodiment, in theabove compounds R⁴ is a C₁₋₄ alkyl radical, and X² is chlorine.Commercially available compounds include triethyl aluminum (TEAL),diethyl aluminum chloride (DEAC), dibutyl magnesium ((Bu)₂Mg), and butylethyl magnesium (BuEtMg or BuMgEt). Alkylaluminoxanes can also be usedas alkylators.

The ionic activator may be selected from: (i) compounds of the formula[R⁵]⁺[B(R⁶)₄]⁻ wherein B is a boron atom, R⁵ is a cyclic C₅₋₇ aromaticcation or a triphenyl methyl cation and each R⁶ is independentlyselected from phenyl radicals which are unsubstituted or substitutedwith from 3 to 5 substituents selected from a fluorine atom, a C₁₋₄alkyl and C₁₋₄ alkoxy radical which is unsubstituted or substituted by afluorine atom; and a silyl radical of the formula —Si—(R⁷)₃; whereineach R⁷ is independently selected from a hydrogen atom and a C₁₋₄ alkylradical; and (ii) compounds of the formula [(R⁸)_(t)ZH]⁺[B(R⁶)₄]⁻wherein B is a boron atom, H is a hydrogen atom, Z is a nitrogen atom orphosphorus atom, t is 2 or 3 and R⁸ is selected from C₁₋₈ alkyl radicalsand a phenyl radical which is unsubstituted or substituted by up tothree C₁₋₄ alkyl radicals; or one R⁸ taken together with the nitrogenatom may form an anilinium radical and R⁶ is as defined above; and (iii)compounds of the formula B(R⁶)₃ wherein R⁶ is as defined above.

In the above compounds R⁶ may be a pentafluorophenyl radical, and R⁵ isa triphenylmethyl cation, Z is a nitrogen atom and R⁸ is a C₁₋₄ alkylradical or R⁸ taken together with the nitrogen atom forms an aniliniumradical which is substituted by two C₁₋₄ alkyl radicals.

Examples of compounds capable of ionizing the phosphinimine catalystinclude the following compounds: triethylammonium tetra(phenyl)boron,tripropylammonium tetra(phenyl)boron, tri(n-butyl)ammoniumtetra(phenyl)boron, trimethylammonium tetra(p-tolyl)boron,trimethylammonium tetra(o-tolyl)boron, tributylammoniumtetra(pentafluorophenyl)boron, tripropylammoniumtetra(o,p-dimethylphenyl)boron, tributylammoniumtetra(m,m-dimethylphenyl)boron, tributylammoniumtetra(p-trifluoromethylphenyl)boron, tributylammoniumtetra(pentafluorophenyl)boron, tri(n-butyl)ammonium tetra(o-tolyl)boron,N,N-dimethylanilinium tetra(phenyl)boron, N,N-diethylaniliniumtetra(phenyl)boron, N,N-diethylanilinium tetra(phenyl)n-butylboron,N,N-2,4,6-pentamethylanilinium tetra(phenyl)boron,di-(isopropyl)ammonium tetra(pentafluorophenyl)boron,dicyclohexylammonium tetra(phenyl)boron, triphenylphosphoniumtetra)phenyl)boron, tri(methylphenyl)phosphonium tetra(phenyl)boron,tri(dimethylphenyl)phosphonium tetra(phenyl)boron, tropilliumtetrakispentafluorophenyl borate, triphenylmethyliumtetrakispentafluorophenyl borate,benzene(diazonium)tetrakispentafluorophenyl borate, tropilliumphenyltrispentafluorophenyl borate, triphenylmethyliumphenyl-trispentafluorophenyl borate, benzene(diazonium)phenyltrispentafluorophenyl borate, tropilliumtetrakis(2,3,5,6-tetrafluorophenyl)borate, triphenylmethyliumtetrakis(2,3,5,6-tetrafluorophenyl)borate, benzene(diazonium)tetrakis(3,4,5-trifluorophenyl)borate, tropilliumtetrakis(3,4,5-trifluorophenyl)borate, benzene(diazonium)tetrakis(3,4,5-trifluorophenyl)borate, tropilliumtetrakis(1,2,2-trifluoroethenyl)borate, trophenylmethyliumtetrakis(1,2,2-trifluoroethenyl)borate, benzene(diazonium)tetrakis(1,2,2-trifluoroethenyl)borate, tropilliumtetrakis(2,3,4,5-tetrafluorophenyl)borate, triphenylmethyliumtetrakis(2,3,4,5-tetrafluorophenyl)borate, and benzene(diazonium)tetrakis(2,3,4,5-tetrafluorophenyl)borate.

Commercially available activators which are capable of ionizing thephosphinimine catalyst include:

N,N-dimethylaniliniumtetrakispentafluorophenyl borate(“[Me₂NHPh][B(C₆F₅)₄]”); triphenylmethylium tetrakispentafluorophenylborate (“[Ph₃C][B(C₆F₅)₄]”); and trispentafluorophenyl boron.

In an embodiment of the invention, the ionic activator compounds may beused in amounts which provide a molar ratio of group 4 transition metalto boron that will be from about 1:1 to about 1:6.

Optionally, mixtures of alkylaluminoxanes and ionic activators can beused as activators for the phosphinimine catalyst.

In one embodiment, the polymerization catalyst system will comprise aninert support (note: the terms “support” and “inert support” are usedinterchangeably in the present invention). In a particular embodiment ofthe invention, the polymerization catalyst system comprises aphosphinimine catalyst which is supported on an inert support.

The inert support can be any support known in the art to be suitable foruse with polymerization catalysts. For example the support can be anyporous or non-porous support material, such as talc, inorganic oxides,inorganic chlorides, aluminophosphates (i.e., AlPO₄) and polymersupports (e.g., polystyrene, etc). Hence, supports include Group 2, 3,4, 5, 13 and 14 metal oxides generally, such as silica, alumina,silica-alumina, magnesium oxide, magnesium chloride, zirconia, titania,clay (e.g., montmorillonite) and mixtures thereof.

Agglomerate supports such as agglomerates of silica and clay may also beused as a support in the current invention.

Supports are generally used in calcined form. An inorganic oxidesupport, for example, will contain acidic surface hydroxyl groups whichwill react with a polymerization catalyst. Prior to use, the inorganicoxide may be dehydrated to remove water and to reduce the concentrationof surface hydroxyl groups. Calcination or dehydration of a support iswell known in the art. In some embodiments of the invention, the supportis calcined at temperatures above about 200° C., or above about 300° C.,or above about 400° C., or above about 500° C. In other embodiments, thesupport is calcined at from about 500° C. to about 1000° C., or fromabout 600° C. to about 900° C. The resulting support may be free ofadsorbed water and may have a surface hydroxyl content from about 0.1 toabout 5 mmol/g of support, or from about 0.5 to about 3 mmol/g. Theamount of hydroxyl groups in a silica support may be determinedaccording to the method disclosed by J. B. Peri and A. L. Hensley Jr.,in J. Phys. Chem., 72 (8), 1968, pg 2926.

The support material, especially an inorganic oxide, typically has asurface area of from about 10 to about 700 m²/g, a pore volume in therange from about 0.1 to about 4.0 cc/g, and an average particle size offrom about 5 to about 500 μm. In one embodiment, the support materialhas a surface area of from about 50 to about 500 m²/g, a pore volume inthe range from about 0.5 to about 3.5 cc/g and an average particle sizeof from about 10 to about 200 μm. In another embodiment the supportmaterial has a surface area of from about 100 to about 400 m²/g, a porevolume in the range from about 0.8 to about 3.0 cc/g and an averageparticle size of from about 5 to about 100 μm.

The support material, especially an inorganic oxide, typically has anaverage pore size (i.e., pore diameter) of from about 10 to about 1000Angstroms (Å). In another embodiment, the support material has anaverage pore size of from about 50 to about 500 Å. In anotherembodiment, the support material has an average pore size of from about75 to about 350 Å.

The surface area and pore volume of a support may be determined bynitrogen adsorption according to B.E.T. techniques, which are well knownin the art and are described in the Journal of the American ChemicalSociety, 1938, v 60, pg 309-319.

A silica support which is suitable for use has a high surface area andis amorphous. By way of example only, useful silicas are commerciallyavailable under the trademark of Sylopol® 958, 955 and 2408 by theDavison Catalysts, a Division of W. R. Grace and Company and ES-70W byIneos Silica.

Agglomerate supports comprising a clay mineral and an inorganic oxide,may be prepared using a number techniques well known in the artincluding pelletizing, extrusion, drying or precipitation, spray-drying,shaping into beads in a rotating coating drum, and the like. Anodulization technique may also be used. Methods to make agglomeratesupports comprising a clay mineral and an inorganic oxide includespray-drying a slurry of a clay mineral and an inorganic oxide. Methodsto make agglomerate supports comprising a clay mineral and an inorganicoxide are disclosed in U.S. Pat. Nos. 6,686,306; 6,399,535; 6,734,131;6,559,090 and 6,958,375.

A useful agglomerate of clay and inorganic oxide may have the followingproperties: a surface area of from about 20 to about 800 m²/g, or fromabout 50 to about 600 m²/g; particles with a bulk density of from about0.15 to about 1 g/ml, or from about 0.20 to about 0.75 g/ml; an averagepore diameter of from about 30 to about 300 Angstroms (Å), or from about60 to about 150 Å; a total pore volume of from about 0.10 to about 2.0cc/g, or from about 0.5 to about 1.8 cc/g; and an average particle sizeof from about 4 to about 250 microns (μm), or from about 8 to about 100microns.

Alternatively, a support, for example a silica support, may be treatedwith one or more salts of the type: Zr(SO₄)₂.4H₂O, ZrO(NO₃)₂, andFe(NO₃)₃ as taught in co-pending Canadian Patent Application No.2,716,772. Supports that have been otherwise chemically treated are alsocontemplated for use with the catalysts and processes of the presentinvention.

The present invention is not limited to any particular procedure forsupporting a phosphinimine catalyst or other catalyst system components.Processes for depositing such catalysts as well as an activator on asupport are well known in the art (for some non-limiting examples ofcatalyst supporting methods, see “Supported Catalysts” by James H. Clarkand Duncan J. Macquarrie, published online Nov. 15, 2002 in theKirk-Othmer Encyclopedia of Chemical Technology Copyright© 2001 by JohnWiley & Sons, Inc.; for some non-limiting methods to support an singlesite catalysts see U.S. Pat. No. 5,965,677). For example, aphosphinimine catalyst may be added to a support by co-precipitationwith the support material. The activator can be added to the supportbefore and/or after the phosphinimine catalyst or together with thephosphinimine catalyst. Optionally, the activator can be added to asupported phosphinimine catalyst in situ or a phosphinimine catalyst maybe added to the support in situ or a phosphinimine catalyst can be addedto a supported activator in situ. A phosphinimine catalyst may beslurried or dissolved in a suitable diluent or solvent and then added tothe support. Suitable solvents or diluents include but are not limitedto hydrocarbons and mineral oil. A phosphinimine catalyst for example,may be added to the solid support, in the form or a solid, solution orslurry, followed by the addition of the activator in solid form or as asolution or slurry. Phosphinimine catalyst, activator, and support canbe mixed together in the presence or absence of a solvent.

A “catalyst modifier” made also be added to the phosphinimine basedcatalyst system and is a compound which, when added to a polymerizationcatalyst system or used in the presence of the same in appropriateamounts, can reduce, prevent or mitigate at least one: of fouling,sheeting, temperature excursions, and static level of a material inpolymerization reactor; can alter catalyst kinetics; and/or can alterthe properties of copolymer product obtained in a polymerizationprocess.

Non limiting examples of catalyst modifiers which can be used areKemamine AS990™. Kemamine AS650™, Armostat-1800™, bis-hydroxy-cocoamine,2,2′-octadecyl-amino-bisethanol, and Atmer-163™.

Other catalyst modifiers may be used and include compounds such ascarboxylate metal salts (see U.S. Pat. Nos. 7,354,880; 6,300,436;6,306,984; 6,391,819; 6,472,342 and 6,608,153 for examples),polysulfones, polymeric polyamines and sulfonic acids (see U.S. Pat.Nos. 6,562,924; 6,022,935 and 5,283,278 for examples).Polyoxyethylenealkylamines, which are described in for example inEuropean Pat. Appl. No. 107,127, may also be used. Further catalystmodifiers include aluminum stearate and aluminum oleate. Catalystmodifiers are supplied commercially under the trademarks OCTASTAT™ andSTADIS™. The catalyst modifier STADIS is described in U.S. Pat. Nos.7,476,715; 6,562,924 and 5,026,795 and is available from Octel Starreon.STADIS generally comprises a polysulfone copolymer, a polymeric amineand an oil soluble sulfonic acid.

A long chain amine type catalyst modifier may be added to a reactor zone(or associated process equipment) separately from the polymerizationcatalyst system, as part of the polymerization catalyst system, or bothas described in co-pending CA Pat. Appl. No. 2,742,461. The long chainamine can be a long chain substituted monoalkanolamine, or a long chainsubstituted dialkanolamine as described in co-pending CA Pat. Appl. No.2,742,461, which is incorporated herein in full.

Detailed descriptions of slurry polymerization processes are widelyreported in the patent literature. For example, particle formpolymerization, or a slurry process where the temperature is kept belowthe temperature at which the polymer goes into solution is described inU.S. Pat. No. 3,248,179. Other slurry processes include those employinga loop reactor and those utilizing a plurality of stirred reactors inseries, parallel, or combinations thereof. Non-limiting examples ofslurry processes include continuous loop or stirred tank processes.Further examples of slurry processes are described in U.S. Pat. No.4,613,484.

Slurry phase polymerization processes are conducted in the presence of ahydrocarbon diluent such as an alkane (including isoalkanes), anaromatic or a cycloalkane. The diluent may also be the alpha olefincomonomer used in copolymerizations. Alkane diluents include propane,butanes, (i.e., normal butane and/or isobutane), pentanes, hexanes,heptanes and octanes. The monomers may be soluble in (or miscible with)the diluent, but the polymer is not (under polymerization conditions).The polymerization temperature may be from about 5° C. to about 200° C.,or less than about 120° C. typically from about 10° C. to about 100° C.The reaction temperature is selected so that the ethylene copolymer isproduced in the form of solid particles. The reaction pressure isinfluenced by the choice of diluent and reaction temperature. Forexample, pressures may range from about 15 to about 45 atmospheres(about 220 to about 660 psi or about 1500 to about 4600 kPa) whenisobutane is used as diluent (see, for example, U.S. Pat. No. 4,325,849)to approximately twice that (i.e., from about 30 to about 90atmospheres-about 440 to about 1300 psi or about 3000 to about 9100 kPa)when propane is used (see U.S. Pat. No. 5,684,097). The pressure in aslurry process is kept sufficiently high to keep at least part of theethylene monomer in the liquid phase. The reaction typically takes placein a jacketed closed loop reactor having an internal stirrer (e.g., animpeller) and at least one settling leg. Catalyst, monomers and diluentsare fed to the reactor as liquids or suspensions. The slurry circulatesthrough the reactor and the jacket is used to control the temperature ofthe reactor. Through a series of let-down valves the slurry enters asettling leg and then is let down in pressure to flash the diluent andunreacted monomers and recover the polymer generally in a cyclone. Thediluent and unreacted monomers are recovered and recycled back to thereactor.

Solution processes for the homopolymerization or copolymerization ofethylene are well known in the art. These processes are conducted in thepresence of an inert hydrocarbon solvent typically a C₅₋₁₂ hydrocarbonwhich may be unsubstituted or substituted by a C₁₋₄ alkyl group, such aspentane, methyl pentane, hexane, heptane, octane, cyclohexane,methylcyclohexane and hydrogenated naphtha. An example of a suitablesolvent which is commercially available is “Isopar E” (C₈₋₁₂ aliphaticsolvent, Exxon Chemical Co.).

The polymerization temperature in a conventional solution process isfrom about 80 to about 300° C. (or from about 120 to about 250° C.).However, as is illustrated in the Examples, the polymerizationtemperature for the process of this invention can be above 160° C. Theupper temperature limit will be influenced by considerations which arewell known to those skilled in the art, such as a desire to maximizeoperating temperature (so as to reduce solution viscosity) while stillmaintaining good polymer properties (as increased polymerizationtemperatures generally reduce the molecular weight of the polymer). Ingeneral, the upper polymerization temperature may be between about 200and about 300° C. (or about 220 to about 250° C.). One reaction processis a “medium pressure process”, meaning that the pressure in the reactoris less than about 6,000 psi (about 42,000 kiloPascals or kPa).Pressures may range from about 10,000 to about 40,000 kPa, or from about2,000 to about 3,000 psi (about 14,000 to about 22,000 kPa).

A gas phase polymerization process is commonly carried out in afluidized bed reactor. Such gas phase processes are widely described inthe literature (see for example U.S. Pat. Nos. 4,543,399, 4,588,790,5,028,670, 5,317,036, 5,352,749, 5,405,922, 5,436,304, 5,453,471,5,462,999, 5,616,661 and 5,668,228). In general, a fluidized bed gasphase polymerization reactor employs a “bed” of polymer and catalystwhich is fluidized by a flow of monomer, comonomer and other optionalcomponents which are at least partially gaseous. Heat is generated bythe enthalpy of polymerization of the monomer (and comonomers) flowingthrough the bed. Un-reacted monomer, comonomer and other optionalgaseous components exit the fluidized bed and are contacted with acooling system to remove this heat. The cooled gas stream, includingmonomer, comonomer and optional other components (such as condensableliquids), is then re-circulated through the polymerization zone,together with “make-up” monomer (and comonomer) to replace that whichwas polymerized on the previous pass. Simultaneously, polymer product iswithdrawn from the reactor. As will be appreciated by those skilled inthe art, the “fluidized” nature of the polymerization bed helps toevenly distribute/mix the heat of reaction and thereby minimize theformation of localized temperature gradients.

The reactor pressure in a gas phase process may vary from aboutatmospheric to about 600 psig. In another embodiment, the pressure canrange from about 100 psig (about 690 kPa) to about 500 psig (about 3448kPa). In another embodiment, the pressure can range from about 200 psig(about 1379 kPa) to about 400 psig (about 2759 kPa). In anotherembodiment, the pressure can range from about 250 psig (about 1724 kPa)to about 350 psig (about 2414 kPa).

The reactor temperature in a gas phase process may vary according to theheat of polymerization as described above. In a one embodiment, thereactor temperature can be from about 30° C. to about 130° C. In anotherembodiment, the reactor temperature can be from about 60° C. to about120° C. In yet another embodiment, the reactor temperature can be fromabout 70° C. to about 110° C. In still yet another embodiment, thetemperature of a gas phase process can be from about 70° C. to about100° C.

The fluidized bed process described above is well adapted for thepreparation of polyethylene but other monomers (i.e., comonomers) mayalso be employed. Monomers and comonomers include ethylene and C₃₋₁₂alpha olefins respectively, where C₃₋₁₂ alpha olefins are unsubstitutedor substituted by up to two C₁₋₆ alkyl radicals, C₈₋₁₂ vinyl aromaticmonomers which are unsubstituted or substituted by up to twosubstituents selected from C₁₋₄ alkyl radicals, C₄₋₁₂ straight chaineddiolefins, and C₄₋₁₂ cyclic diolefins, each of which are unsubstitutedor substituted by a C₁₋₄ alkyl radical. Illustrative non-limitingexamples of such alpha-olefins are one or more of propylene, 1-butene,1-pentene, 1-hexene, 1-octene, and 1-decene, styrene, alpha methylstyrene, p-tert-butyl styrene, and the constrained-ring cyclic olefinssuch as cyclobutene, cyclopentene, dicyclopentadiene norbornene,alkyl-substituted norbornenes, alkenyl-substituted norbornenes and thelike (e.g., 5-methylene-2-norbornene and 5-ethylidene-2-norbornene,bicyclo-(2,2,1)-hepta-2,5-diene).

In one embodiment, the invention is directed toward a polymerizationprocess involving the polymerization of ethylene with one or more ofcomonomer(s) including linear or branched comonomers) having from 3 to30 carbon atoms, for example, 3-12 carbon atoms, or 3 to 8 carbon atoms.

The process is particularly well suited to the copolymerizationreactions involving the polymerization of ethylene in combination withone or more of the comonomers, for example alpha-olefin comonomers suchas propylene, butene-1, pentene-1,4-methylpentene-1, hexene-1, octene-1,decene-1, styrene and cyclic and polycyclic olefins such ascyclopentene, norbornene and cyclohexene or a combination thereof. Othercomonomers for use with ethylene can include polar vinyl monomers,diolefins such as 1,3-butadiene, 1,4-pentadiene, 1,4-hexadiene,1,5-hexadiene, norbornadiene, and other unsaturated monomers includingacetylene and aldehyde monomers. Higher alpha-olefins and polyenes ormacromers can be used also.

In one embodiment, the first polyethylene copolymer comprises ethyleneand an alpha-olefin having from 3 to 15 carbon atoms, or 4 to 12 carbonatoms, or 4 to 10 carbon atoms.

In an embodiment of the invention, ethylene comprises at least about 75wt % of the total weight of monomer (i.e., ethylene) and comonomer(i.e., alpha olefin) that is fed to a polymerization reactor.

In an embodiment of the invention, ethylene comprises at least about 85wt % of the total weight of monomer (i.e., ethylene) and comonomer(i.e., alpha olefin) that is fed to a polymerization reactor.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer of ethylene and an alpha-olefin having from 3-8 carbon atomsand is made in a single reactor in the presence of a polymerizationcatalyst system comprising a phosphinimine catalyst, a support and acatalyst activator.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer of ethylene and an alpha-olefin having from 3-8 carbon atomsand is made in a single gas phase reactor in the presence of apolymerization catalyst system comprising a phosphinimine catalyst, asupport and a catalyst activator.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer of ethylene and an alpha-olefin having from 3-8 carbon atomsand is made in a single gas phase reactor in the presence of apolymerization catalyst system comprising a phosphinimine catalyst, asupport and a catalyst activator, wherein the phosphinimine catalyst hasthe formula:(1-R²-Indenyl)Ti(N═P(t-Bu)₃)X₂;

wherein R² is a substituted or unsubstituted alkyl group, a substitutedor an unsubstituted aryl group, or a substituted or unsubstituted benzylgroup, wherein substituents for the alkyl, aryl or benzyl group areselected from alkyl, aryl, alkoxy, aryloxy, alkylaryl, arylalkyl andhalide substituents; and wherein X is an activatable ligand.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer of ethylene and an alpha-olefin having from 3-8 carbon atomsand is made in a single gas phase reactor with a polymerization catalystsystem comprising: a phosphinimine catalyst; an alkylaluminoxanecocatalyst; and a support.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer of ethylene and an alpha-olefin having from 3-8 carbon atomsand is made in a single gas phase reactor with a polymerization catalystsystem comprising: a phosphinimine catalyst; an alkylaluminoxanecocatalyst; a support; and a catalyst modifier.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer of ethylene and an alpha-olefin having from 3-8 carbon atomsand is made in a single gas phase reactor with a polymerization catalystsystem comprising: a phosphinimine catalyst having the formula(1-R²-Ind)Ti(N═P(t-Bu)₃)X₂ where R² is an alkyl group, an aryl group ora benzyl group wherein each of the alkyl group, the aryl group, or thebenzyl group may be unsubstituted or substituted by at least one halideatom, and where X is an activatable ligand; and an activator.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer of ethylene and an alpha-olefin having from 3-8 carbon atomsand is made in a single gas phase reactor with a polymerization catalystsystem comprising: a phosphinimine catalyst having the formula(1-R²-Ind)Ti(N═P(t-Bu)₃)X₂ where R² is an alkyl group, an aryl group ora benzyl group wherein each of the alkyl group, the aryl group, or thebenzyl group may be unsubstituted or substituted by at least one halideatom, where X is an activatable ligand; an activator; and an inertsupport.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer of ethylene and an alpha-olefin having from 3-8 carbon atomsand is made in a single gas phase reactor with a polymerization catalystsystem comprising: a phosphinimine catalyst having the formula(1-R²-Ind)Ti(N═P(t-Bu)₃)X₂ where R² is an alkyl group, an aryl group ora benzyl group wherein each of the alkyl group, the aryl group, or thebenzyl group may be unsubstituted or substituted by at least one halideatom, where X is an activatable ligand; an activator; an inert support;and a catalyst modifier.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer is a copolymer of ethylene and an alpha-olefin having from 3-8carbon atoms and is made in a single gas phase reactor with apolymerization catalyst system comprising: a phosphinimine catalysthaving the formula (1-C₆F₅CH₂-Ind)Ti(N═P(t-Bu)₃)X₂ where X is anactivatable ligand; an activator; and an inert support.

In an embodiment of the invention, the first polyethylene copolymer is acopolymer is a copolymer of ethylene and an alpha-olefin having from 3-8carbon atoms and is made in a single gas phase reactor with apolymerization catalyst system comprising: a phosphinimine catalysthaving the formula (1-C₆F₅CH₂-Ind)Ti(N═P(t-Bu)₃)X₂ where X is anactivatable ligand; an activator; an inert support; and a catalystmodifier.

The polymerization catalyst system may be fed to a reactor system in anumber of ways. If the phosphinimine catalyst is supported on a suitablesupport, the catalyst may be fed to a reactor in dry mode using a drycatalyst feeder, examples of which are well known in the art.Alternatively, a supported phosphinimine catalyst may be fed to areactor as a slurry in a suitable diluent. If the phosphinimine catalystis unsupported, the catalyst can be fed to a reactor as a solution or asa slurry in a suitable solvent or diluents. Polymerization catalystsystem components, which may include a phosphinimine catalyst, anactivator, a scavenger, an inert support, and a catalyst modifier, maybe combined prior to their addition to a polymerization zone, or theymay be combined on route to a polymerization zone. To combinepolymerization catalyst system components on route to a polymerizationzone they can be fed as solutions or slurries (in suitable solvents ordiluents) using various feed line configurations which may becomecoterminous before reaching the reactor. Such configurations can bedesigned to provide areas in which catalyst system components flowing toa reactor can mix and react with one another over various “hold up”times which can be moderated by changing the solution or slurry flowrates of the catalyst system components.

Optionally, scavengers are added to a polymerization process. Scavengersare well known in the art.

In an embodiment of the invention, scavengers are organoaluminumcompounds having the formula: Al³(X³)_(n)(X⁴)_(3-n), where (X³) is ahydrocarbyl having from 1 to about 20 carbon atoms; (X⁴) is selectedfrom alkoxide or aryloxide, any one of which having from 1 to about 20carbon atoms; halide; or hydride; and n is a number from 1 to 3,inclusive; or alkylaluminoxanes having the formula: R³₂Al¹O(R³Al¹O)_(m)Al¹R³ ₂

wherein each R³ is independently selected from C₁₋₂₀ hydrocarbylradicals and m is from 3 to 50. Some non-limiting examples of usefulscavengers include triisobutylaluminum, triethylaluminum,trimethylaluminum or other trialkylaluminum compounds.

The scavenger may be used in any suitable amount but by way ofnon-limiting examples only, can be present in an amount to provide amolar ratio of Al:M (where M is the metal of the organometalliccompound) of from about 20 to about 2000, or from about 50 to about1000, or from about 100 to about 500. Generally the scavenger is addedto the reactor prior to the catalyst and in the absence of additionalpoisons and over time declines to about 0, or is added continuously.

Optionally, the scavengers may be independently supported. For example,an inorganic oxide that has been treated with an organoaluminum compoundor alkylaluminoxane may be added to the polymerization reactor. Themethod of addition of the organoaluminum or alkylaluminoxane compoundsto the support is not specifically defined and is carried out byprocedures well known in the art.

Preparation of the Polymer Blend

The polymer blend can be formed using conventional equipment andmethods, such as by dry blending the individual components andsubsequently melt mixing in a mixer or by mixing the components togetherdirectly in a mixer, such as, for example, a Banbury mixer, a Haakemixer, a Brabender internal mixer, or a single or twin-screw extruder,which can include a compounding extruder and a side-arm extruder useddirectly downstream of a polymerization process. A mixture or blend ofthe first and second polyethylene copolymers can be indicated by theuniformity of the morphology of the composition. In another example, thepolymer blend can be produced in situ using a multistage polymerizationreactor arrangement and process. In a multistage reactor arrangement twoor more reactors can be connected in series where a mixture of a firstpolymer and catalyst can be transferred from a first reactor to a secondreactor where a second polymer can be produced and blended in situ withthe first polymer. A multi-stage polymerization reactor and methods forusing the same can be similar to that discussed and described in forexample, U.S. Pat. No. 5,677,375. Blending of polymer components whilein solution is also contemplated for use in the present invention.

The polymer blend can include at least about 1 percent by weight (wt %)and up to about 99 wt % of the first polyethylene copolymer and at leastabout 1 wt % and up to about 99 wt % of the second polyethylenecopolymer, based on the total weight of the first and secondpolyethylene copolymers.

In embodiments of the invention, the amount of the first polyethylenecopolymer in the polymer blend will be in the range from a low of about5 wt %, or about 10 wt %, or about 15 wt %, or about 20 wt %, or about30 wt %, or about 40 wt % to a high of about 60 wt %, or about 70 wt %,or about 80 wt %, or about 90 wt %, or about 95 wt %, based on the totalweight of the first and second polyethylene copolymers.

In embodiments of the invention, the amount of the first polyethylenecopolymer in the polymer blend will be in the range of from about 1 wt %to about 50 wt %, or from about 5 wt % to about 50 wt %, or from about7.5 wt % to about 50 wt %, or from about 10 wt % to about 50 wt %, orfrom about 12.5 wt % to about 50 wt %, or from about 12.5 wt % to about40 wt %, or from about 15 wt % to about 40 wt %, or from about 10 wt %to about 35 wt %, or from about 10 wt % to about 45 wt %, or from about10 wt % to about 30 wt %, or from about 7.5 wt % to about 30 wt %, orfrom about 5 wt % to about 35 wt %, or from about 5 wt % to about 30 wt%, or from about 5 wt % to about 25 wt %, or from about 1 wt % to about25 wt %, based on the total weight of the first and second polyethylenecopolymers. In further embodiments of the invention, the amount of thefirst polyethylene copolymer in the polymer blend can be at least about5 wt %, or at least about 10 wt %, at least about 15 wt %, or at leastabout 20 wt %, or at least about 25 wt %, or at least about 30 wt %, orat least about 35 wt %, but less than about 50 wt %, based on the totalweight of the first and second polyethylene copolymers.

In an embodiments of the invention, the amount of the first polyethylenecopolymer in the polymer blend can be at least about 50 wt %, or atleast about 60 wt %, at least about 70 wt %, or at least about 80 wt %,or at least about 90 wt % but less than about 100 wt %, based on thetotal weight of the first and second polyethylene copolymers.

In an embodiment of the invention, the polymer blend comprises fromabout 1 to about 99 wt % of a first polyethylene copolymer and 99 to 1wt % of a second polyethylene copolymer, based on the total weight ofthe first and second polyethylene copolymers.

In an embodiment of the invention, the polymer blend comprises fromabout 5 to about 95 wt % of a first polyethylene copolymer and fromabout 95 to about 5 wt % of a second polyethylene copolymer, based onthe total weight of the first and second polyethylene copolymers.

In an embodiment of the invention, the polymer blend comprises fromabout 1 to about 50 wt % of a first polyethylene copolymer and fromabout 99 to about 50 wt % of a second polyethylene copolymer, based onthe total weight of the first and second polyethylene copolymers.

In an embodiment of the invention, the polymer blend comprises fromabout 5 to about 50 wt % of a first polyethylene copolymer and fromabout 95 to about 50 wt % of a second polyethylene copolymer, based onthe total weight of the first and second polyethylene copolymers.

In an embodiment of the invention, the polymer blend comprises fromabout 95 to about 50 wt % of a first polyethylene copolymer and fromabout 5 to about 50 wt % of a second polyethylene copolymer, based onthe total weight of the first and second polyethylene copolymers.

In an embodiment of the invention, the polymer blend comprises fromabout 95 to about 60 wt % of a first polyethylene copolymer and fromabout 5 to about 40 wt % of a second polyethylene copolymer, based onthe total weight of the first and second polyethylene copolymers.

In an embodiment of the invention, the polymer blend comprises fromabout 90 to about 50 wt % of a first polyethylene copolymer and fromabout 10 to about 50 wt % of a second polyethylene copolymer, based onthe total weight of the first and second polyethylene copolymers.

Additives

The polymer blend or the polymer blend components (i.e., the firstand/or second polyethylene copolymers) of the current invention, mayalso contain additives, such as for example, primary antioxidants (suchas hindered phenols, including vitamin E); secondary antioxidants (suchas phosphites and phosphonites); nucleating agents, plasticizers orprocess aids (such as fluoroelastomer and/or polyethylene glycol boundprocess aid), acid scavengers, stabilizers, anticorrosion agents,blowing agents, other ultraviolet light absorbers such as chain-breakingantioxidants, etc., quenchers, antistatic agents, slip agents,anti-blocking agent, pigments, dyes and fillers and cure agents such asperoxide.

These and other common additives in the polyolefin industry may bepresent in polymer blend (and/or the first and/or second polyethylenecopolymers) at from about 0.01 to about 50 wt % in one embodiment, andfrom about 0.1 to about 20 wt % in another embodiment, and from about 1to about 5 wt % in yet another embodiment, wherein a desirable range maycomprise any combination of any upper wt % limit with any lower wt %limit.

In an embodiment of the invention, antioxidants and stabilizers such asorganic phosphites and phenolic antioxidants may be present in thepolymer blend (and/or the first and/or second polyethylene copolymers)in from about 0.001 to about 5 wt % in one embodiment, and from about0.01 to about 0.8 wt % in another embodiment, and from about 0.02 toabout 0.5 wt % in yet another embodiment. Non-limiting examples oforganic phosphites that are suitable aretris(2,4-di-tert-butylphenyl)phosphite (IRGAFOS 168) and tris(nonylphenyl)phosphite (WESTON 399). Non-limiting examples of phenolicantioxidants include octadecyl 3,5 di-t-butyl-4-hydroxyhydrocinnamate(IRGANOX 1076) and pentaerythrityltetrakis(3,5-di-tert-butyl-4-hydroxyphenyl)propionate (IRGANOX 1010);and 1,3,5-Tri(3,5-di-tert-butyl-4-hydroxybenzyl-isocyanurate (IRGANOX3114).

Fillers may be present in the polymer blend (and/or the first and/orsecond polyethylene copolymers) in from about 0.1 to about 50 wt % inone embodiment, and from about 0.1 to about 25 wt % of the compositionin another embodiment, and from about 0.2 to about 10 wt % in yetanother embodiment. Fillers include but are not limited to titaniumdioxide, silicon carbide, silica (and other oxides of silica,precipitated or not), antimony oxide, lead carbonate, zinc white,lithopone, zircon, corundum, spinel, apatite, Barytes powder, bariumsulfate, magnesiter, carbon black, dolomite, calcium carbonate, talc andhydrotalcite compounds of the ions Mg, Ca, or Zn with Al, Cr or Fe andCO₃ and/or HPO₄, hydrated or not; quartz powder, hydrochloric magnesiumcarbonate, glass fibers, clays, alumina, and other metal oxides andcarbonates, metal hydroxides, chrome, phosphorous and brominated flameretardants, antimony trioxide, silica, silicone, and blends thereof.These fillers may particularly include any other fillers and porousfillers and supports which are known in the art.

Fatty acid salts may also be present in the polymer blends (and/or thefirst and/or second polyethylene copolymers). Such salts may be presentfrom about 0.001 to about 2 wt % in the polymer blend or in the polymerblend components in one embodiment, and from about 0.01 to about 1 wt %in another embodiment. Examples of fatty acid metal salts include lauricacid, stearic acid, succinic acid, stearyl lactic acid, lactic acid,phthalic acid, benzoic acid, hydroxystearic acid, ricinoleic acid,naphthenic acid, oleic acid, palmitic acid, and erucic acid, suitablemetals including Li, Na, Mg, Ca, Sr, Ba, Zn, Cd, Al, Sn, Pb and soforth. Desirable fatty acid salts are selected from magnesium stearate,calcium stearate, sodium stearate, zinc stearate, calcium oleate, zincoleate, and magnesium oleate.

With respect to the physical process of introducing to the polymer blend(and/or the first and/or second polyethylene copolymers) one or moreadditives, sufficient mixing should take place to assure that a uniformblend will be produced prior to conversion into a finished product. Thepolymer blend (and/or the first and/or second polyethylene copolymers)can be in any physical form when used to blend with the one or moreadditives. In one embodiment, reactor granules, defined as the granulesof the polymer blend (and/or the first and/or second polyethylenecopolymers) that are isolated and used to blend with the additives. Thereactor granules have an average diameter of from about 10 μm to about 5mm, and from about 50 μm to about 10 mm in another embodiment.Alternately, the polymer blend or its components may be in the form ofpellets, such as, for example, having an average diameter of from about1 mm to about 6 mm that are formed from melt extrusion of the reactorgranules.

One method of blending the additives with the polymer blend (and/or thefirst and/or second polyethylene copolymers) is to contact thecomponents in a tumbler or other physical blending means, the copolymerbeing in the form of reactor granules. This can then be followed, ifdesired, by melt blending in an extruder. Another method of blending thecomponents is to melt blend the polymer blend or polymer blend componentpellets with the additives directly in an extruder, or any other meltblending means.

Film Production

The extrusion-blown film process is a well-known process for thepreparation of plastic film. The process employs an extruder whichheats, melts and conveys the molten plastic (e.g., the polymer blend)and forces it through an annular die. Typical extrusion temperatures arefrom about 330 to about 500° F., especially about 350 to about 460° F.

The polyethylene film is drawn from the die and formed into a tube shapeand eventually passed through a pair of draw or nip rollers. Internalcompressed air is then introduced from a mandrel causing the tube toincrease in diameter forming a “bubble” of the desired size. Thus, theblown film is stretched in two directions, namely in the axial direction(by the use of forced air which “blows out” the diameter of the bubble)and in the lengthwise direction of the bubble (by the action of awinding element which pulls the bubble through the machinery). Externalair is also introduced around the bubble circumference to cool the meltas it exits the die. Film width is varied by introducing more or lessinternal air into the bubble thus increasing or decreasing the bubblesize. Film thickness is controlled primarily by increasing or decreasingthe speed of the draw roll or nip roll to control the draw-down rate.

The bubble is then collapsed into two doubled layers of film immediatelyafter passing through the draw or nip rolls. The cooled film can then beprocessed further by cutting or sealing to produce a variety of consumerproducts. While not wishing to be bound by theory, it is generallybelieved by those skilled in the art of manufacturing blown films thatthe physical properties of the finished films are influenced by both themolecular structure of a polyethylene copolymer and by the processingconditions. For example, the processing conditions are thought toinfluence the degree of molecular orientation (in both the machinedirection and the axial or cross direction).

A balance of “machine direction” (“MD”) and “transverse direction”(“TD”—which is perpendicular to MD) molecular orientation is generallyconsidered desirable for the films associated with the invention (forexample, Dart Impact strength, Machine Direction and TransverseDirection tear properties).

Thus, it is recognized that these stretching forces on the “bubble” canaffect the physical properties of the finished film. In particular, itis known that the “blow up ratio” (i.e. the ratio of the diameter of theblown bubble to the diameter of the annular die) can have a significanteffect upon the dart impact strength and tear strength of the finishedfilm.

The above description relates to the preparation of monolayer films.Multilayer films may be prepared by 1) a “co-extrusion” process thatallows more than one stream of molten polymer to be introduced to anannular die resulting in a multi-layered film membrane or 2) alamination process in which film layers are laminated together.

In an embodiment of the invention, the films of this invention areprepared using the above described blown film process.

An alternative process is the so-called cast film process, wherein apolyethylene copolymer (or polymer blend) is melted in an extruder, thenforced through a linear slit die, thereby “casting” a thin flat film.The extrusion temperature for cast film is typically somewhat hotterthan that used in the blown film process (with typically operatingtemperatures of from about 450 to about 550° F.). In general, cast filmis cooled (quenched) more rapidly than blown film.

In an embodiment of the invention, the films of this invention areprepared using a cast film process.

The films of the invention may be single layer or multiple layer films.The multiple layer films may comprise one or more layers formed from thepolymer blend. The films may also have one or more additional layersformed from other materials such as other polymers, linear low densitypolyethylene (LLDPE), medium density polyethylene, polypropylene,polyester, low density polyethylene (HPLDPE), high density polyethylene(HDPE), ethylene vinyl acetate, ethylene vinyl alcohol and the like.

Multiple layer films may be formed by methods well known in the art. Ifall layers are polymer, the polymers may be coextruded through acoextrusion feed block and die assembly to yield a film with two or morelayers adhered together but differing in composition. Multiple layerfilms may also be formed by extrusion coating whereby a substratematerial is contacted with the hot molten polymer as it exits the die.

Polymer Blend Film Properties.

Films can be made from the polymer blends as defined above. Generally,an additive as described above is mixed with the polymer blends prior tofilm production. The polymer blends and films have a balance ofprocessing and mechanical properties as well as good optical properties.Accordingly, in an embodiment of the invention, a ˜1 mil monolayer filmwill have a dart impact strength of ≧ about 250 g/mil, and a about 1% MDsecant modulus of greater than about 140 MPa in combination with goodfilm optical properties.

In embodiments of the invention, the film will have a dart impact of ≧about 220 g/mil, or ≧ about 230 g/mil, or ≧ about 240 g/mil, or ≧ about250 g/mil, or ≧ about 350 g/mil, or ≧ about 400 g/mil, or ≧ about 450g/mil, or ≧ about 500 g/mil, or ≧ about 550 g/mil, or ≧ about 600 g/mil,or ≧ about 650 g/mil, or ≧ about 700 g/mil. In another embodiment of theinvention, the film will have a dart impact of from about 230 g/mil toabout 900 g/mil. In another embodiment of the invention, the film willhave a dart impact of from about 230 g/mil to about 800 g/mil. Inanother embodiment of the invention, the film will have a dart impact offrom about 250 g/mil to about 750 g/mil. In a further embodiment of theinvention, the film will have dart impact of from about 300 g/mil toabout 750 g/mil. In a further embodiment of the invention, the film willhave dart impact of from about 350 g/mil to about 750 g/mil. In afurther embodiment of the invention, the film will have dart impact offrom about 400 g/mil to about 750 g/mil. In a further embodiment of theinvention, the film will have dart impact of from about 450 g/mil toabout 750 g/mil. In yet another embodiment of the invention, the filmwill have dart impact of from about 500 g/mil to about 750 g/mil. In yetanother embodiment of the invention, the film will have dart impact offrom about 550 g/mil to about 750 g/mil. In still yet another embodimentof the invention, the film will have dart impact of from about 600 g/milto about 750 g/mil. In a further embodiment of the invention, the filmwill have dart impact of from about 650 g/mil to about 750 g/mil. In afurther embodiment of the invention, the film will have dart impact offrom about 650 g/mil to about 800 g/mil.

In embodiments of the invention, the film will have a ratio of MD tearto TD tear (MD tear/TD tear) of less than about 0.95, but greater thanabout 0.10, or less than about 0.80, but greater than about 0.10. Inanother embodiment of the invention, the film will have a ratio of MDtear to TD tear of from about 0.10 to about 0.95. In another embodimentof the invention, the film will have a ratio of MD tear to TD tear offrom about 0.10 to about 0.80. In another embodiment of the invention,the film will have a ratio of MD tear to TD tear of from about 0.10 toabout 0.75. In yet another embodiment of the invention, the film willhave a ratio of MD tear to TD tear of from about 0.1 to about 0.70. Instill another embodiment of the invention, the film will have a ratio ofMD tear to TD tear of from about 0.2 to about 0.70. In anotherembodiment of the invention, the film will have a ratio of MD tear to TDtear of from 0.25 to 0.65.

In embodiments of the invention, a ˜1 mil film will have a machinedirection (MD) secant modulus at about 1% strain of ≧ about 120 MPa, or≧ about 130 MPa, or ≧ about 140 MPa, or ≧ about 150 MPa, or ≧ about 160MPa. In an embodiment of the invention, a ˜1 mil film will have amachine direction (MD) secant modulus at about 1% strain of from about120 MPa to about 260 MPa. In an embodiment of the invention, a ˜1 milfilm will have a machine direction (MD) secant modulus at about 1%strain of from about 130 MPa to about 230 MPa. In another embodiment ofthe invention, a ˜1 mil film will have a machine direction (MD) secantmodulus at about 1% strain of from about 130 MPa to about 210 MPa. Inanother embodiment of the invention, a ˜1 mil film will have a machinedirection (MD) secant modulus at about 1% strain of from about 120 MPato about 200 MPa. In another embodiment of the invention, a ˜1 mil filmwill have a machine direction (MD) secant modulus at about 1% strain offrom about 120 MPa to about 190 MPa. In another embodiment of theinvention, a ˜1 mil film will have a machine direction (MD) secantmodulus at about 1% strain of from about 130 MPa to about 180 MPa.

In an embodiment of the invention, a ˜1 mil film will have a transversedirection (TD) secant modulus at about 1% strain of ≧ about 130 MPa, or≧ about 140 MPa, or ≧ about 150 MPa, or ≧ about 160 MPa, or ≧ about 170MPa, or ≧ about 180 MPa, or ≧ about 190 MPa. In an embodiment of theinvention, a ˜1 mil film will have a transverse direction (TD) secantmodulus at about 1% strain of from about 120 MPa to about 280 MPa. In anembodiment of the invention, a ˜1 mil film will have a transversedirection (TD) secant modulus at about 1% strain of from about 120 MPato about 270 MPa. In another embodiment of the invention, a ˜1 mil filmwill have a transverse direction (TD) secant modulus at about 1% strainof from about 120 MPa to about 260 MPa. In another embodiment of theinvention, a ˜1 mil film will have a transverse direction (TD) secantmodulus at about 1% strain of from about 130 MPa to about 240 MPa. Inanother embodiment of the invention, a ˜1 mil film will have atransverse direction (TD) secant modulus at about 1% strain of fromabout 130 MPa to about 220 MPa. In another embodiment of the invention,a ˜1 mil film will have a transverse direction (TD) secant modulus atabout 1% strain of from about 120 MPa to about 220 MPa. In yet anotherembodiment of the invention, a ˜1 mil film will have a transversedirection (TD) secant modulus at about 1% strain of from about 130 MPato about 210 MPa. In yet another embodiment of the invention, a ˜1 milfilm will have a transverse direction (TD) secant modulus at about 1%strain of from about 130 MPa to about 200 MPa. In yet another embodimentof the invention, a ˜1 mil film will have a transverse direction (TD)secant modulus at about 1% strain of from about 130 MPa to about 190MPa.

In an embodiment of the invention, a ˜1 mil film will have a haze ofless than about 15% and a gloss at about 45° of at least about 40. In anembodiment of the invention, a ˜1 mil film will have a haze of less thanabout 15% and a gloss at about 45° of at least about 45. In anembodiment of the invention, a ˜1 mil film will have a haze of less thanabout 12% and a gloss at about 45° of at least about 50. In anembodiment of the invention, a ˜1 mil film will have a haze of less thanabout 12% and a gloss at about 45° of at least about 55. In anembodiment of the invention, a ˜1 mil film will have a haze of less thanabout 10% and a gloss at about 45° of at least about 50. In anembodiment of the invention, a ˜1 mil film will have a haze of less thanabout 10% and a gloss at about 45° of at least about 55. In anembodiment of the invention, a ˜1 mil film will have a haze of less thanabout 10% and a gloss at about 45° of at least 60. In another embodimentof the invention, a ˜1 mil film will have a haze of less than about 7%and a gloss at about 45° of at least about 55. In another embodiment ofthe invention, a ˜1 mil film will have a haze of less than about 7% anda gloss at about 45° of at least about 60. In another embodiment of theinvention, a ˜1 mil film will have a haze of less than about 7% and agloss at about 45° of at least about 65. In another embodiment of theinvention, a ˜1 mil film will have a haze of less than about 7% and agloss at about 45° of at least about 70.

The film may, by way of non-limiting example, have a total thicknessranging from about 0.5 mils to about 4 mils (note: 1 mil=0.0254 mm),which will depend on for example the die gap employed during filmcasting or film blowing.

The above description applies to monolayer films. However, the filmsdisclosed and claimed herein may be used in a multilayer film.Multilayer films can be made using a co-extrusion process or alamination process. In co-extrusion, a plurality of molten polymerstreams are fed to an annular die (or flat cast) resulting in amulti-layered film on cooling. In lamination, a plurality of films arebonded together using, for example, adhesives, joining with heat andpressure and the like. A multilayer film structure may, for example,contain tie layers and/or sealant layers.

The films disclosed and claimed herein may be a skin layer or a corelayer and can be used in at least one or a plurality of layers in amultilayer film. The term “core” or the phrase “core layer”, refers toany internal film layer in a multilayer film. The phrase “skin layer”refers to an outermost layer of a multilayer film (for example, as usedin the production of produce packaging). The phrase “sealant layer”refers to a film that is involved in the sealing of the film to itselfor to another layer in a multilayer film. A “tie layer” refers to anyinternal layer that adheres two layers to one another.

By way of non-limiting example only, the thickness of the multilayerfilms can be from about 0.5 mil to about 10 mil total thickness.

In an embodiment of the invention, a monolayer or multilayer filmstructure comprises at least one layer comprising a polymer blendcomprising the first and second polyethylene copolymers described above.

By way of non-limiting examples, the films can be used for heavy dutybags, shrink film, stretch film, agricultural film, garbage bags andshopping bags. The films can be produced by blow extrusion, castextrusion, co-extrusion and be incorporated also in laminatedstructures.

In an embodiment of the invention, a blown film is provided whichcomprises the polymer blend described above.

In an embodiment of the invention, a cast film is provided whichcomprises the polymer blend described above.

In embodiments of the invention, a stretch film, or a shrink film isprovided which comprises the polymer blend described above.

In embodiments of the invention, a blown film, or a cast film having ahaze of less than about 10% and a gloss at about 45° of greater thanabout 55 is provided which comprises the polymer blend described above.

In an embodiment of the invention, a stretch film or a cast film havinga haze of less than about 10% and a gloss at about 45° of greater thanabout 55 is provided which comprises the polymer blend described above.

The present invention will further be described by reference to thefollowing examples. The following examples are merely illustrative ofthe invention and are not intended to be limiting. Unless otherwiseindicated, all percentages are by weight unless otherwise specified.

EXAMPLES General

All reactions involving air and or moisture sensitive compounds wereconducted under nitrogen using standard Schlenk and cannula techniques,or in a glovebox. Reaction solvents were purified either using thesystem described by Pangborn et. al. in Organometallics 1996, v 15, p.1518 or used directly after being stored over activated 4 Å molecularsieves. The methylaluminoxane used was a 10% MAO solution in toluenesupplied by Albemarle which was used as received. The support used wassilica Sylopol 2408 obtained from W.R. Grace. & Co. The support wascalcined by fluidizing with air at 200° C. for 2 hours followed bynitrogen at 600° C. for 6 hours and stored under nitrogen.

Melt index, I₂, in g/10 min was determined on a Tinius Olsen Plastomer(Model MP993) in accordance with ASTM D1238 condition F at 190° C. witha 2.16 kilogram weight. Melt index, I₁₀, was determined in accordancewith ASTM D1238 condition F at 190° C. with a 10 kilogram weight. Highload melt index, I₂₁, in g/10 min was determined in accordance with ASTMD1238 condition Eat 190° C. with a 21.6 kilogram weight. Melt flow ratioor “MFR” for short (also sometimes called melt index ratio) is I₂₁/I₂.

Polymer density was determined in grams per cubic centimeter (g/cc)according to ASTM D792.

Molecular weight information (M_(w), M_(n) and M_(z) in g/mol) andmolecular weight distribution (M_(w)/M_(n)), and z-average molecularweight distribution (M_(z)/M_(w)) were analyzed by gel permeationchromatography (GPC), using an instrument sold under the trade name“Waters 150c”, with 1,2,4-trichlorobenzene as the mobile phase at 140°C. The samples were prepared by dissolving the polymer in this solventand were run without filtration. Molecular weights are expressed aspolyethylene equivalents with a relative standard deviation of 2.9% forthe number average molecular weight (“Mn”) and 5.0% for the weightaverage molecular weight (“Mw”). Polymer sample solutions (1 to 2 mg/mL)were prepared by heating the polymer in 1,2,4-trichlorobenzene (TCB) androtating on a wheel for 4 hours at 150° C. in an oven. The antioxidant2,6-di-tert-butyl-4-methylphenol (BHT) was added to the mixture in orderto stabilize the polymer against oxidative degradation. The BHTconcentration was 250 ppm. Sample solutions were chromatographed at 140°C. on a PL 220 high-temperature chromatography unit equipped with fourShodex columns (HT803, HT804, HT805 and HT806) using TCB as the mobilephase with a flow rate of 1.0 mL/minute, with a differential refractiveindex (DRI) as the concentration detector. BHT was added to the mobilephase at a concentration of 250 ppm to protect the columns fromoxidative degradation. The sample injection volume was 200 mL. The rawdata were processed with Cirrus GPC software. The columns werecalibrated with narrow distribution polystyrene standards. Thepolystyrene molecular weights were converted to polyethylene molecularweights using the Mark-Houwink equation, as described in the ASTMstandard test method D6474.

The branch frequency of copolymer samples (i.e. the short chainbranching, SCB per 1000 carbons) and the C₆ comonomer content (in wt %)was determined by Fourier Transform Infrared Spectroscopy (FTIR) as perthe ASTM D6645-01 method. A Thermo-Nicolet 750 Magna-IRSpectrophotometer equipped with OMNIC version 7.2a software was used forthe measurements.

The determination of branch frequency as a function of molecular weight(and hence the comonomer distribution) was carried out using hightemperature Gel Permeation Chromatography (GPC) and FT-IR of the eluent.Polyethylene standards with a known branch content, polystyrene andhydrocarbons with a known molecular weight were used for calibration.

Hexane extractables compression molded plaques were determined accordingto ASTM D5227.

To determine the composition distribution breadth index CDBI₅₀, which isalso designated CDBI(50) in the present invention, a solubilitydistribution curve is first generated for the copolymer. This isaccomplished using data acquired from the TREF technique. Thissolubility distribution curve is a plot of the weight fraction of thecopolymer that is solubilized as a function of temperature. This isconverted to a cumulative distribution curve of weight fraction versuscomonomer content, from which the CDBI₅₀ is determined by establishingthe weight percentage of a copolymer sample that has a comonomer contentwithin 50% of the median comonomer content on each side of the median(see WO 93/03093 for the definition of CDBI₅₀). The weight percentage ofcopolymer eluting at from 90-105° C., is determined by calculating thearea under the TREF curve at an elution temperature of from 90 to 105°C. The weight percent of copolymer eluting below at or 40° C. and above100° C. was determined similarly. For the purpose of simplifying thecorrelation of composition with elution temperature, all fractions areassumed to have a Mn≧15,000, where Mn is the number average molecularweight of the fraction. Any low weight fractions present generallyrepresent a trivial portion of the polymer. The remainder of thisdescription and the appended claims maintain this convention of assumingall fractions have Mn≧15,000 in the CDBI₅₀ measurement.

The specific temperature rising elution fractionation (TREF) method usedherein was as follows. Homogeneous polymer samples (pelletized, 50 to150 mg) were introduced into the reactor vessel of acrystallization-TREF unit (Polymer ChAR™). The reactor vessel was filledwith 20 to 40 ml 1,2,4-trichlorobenzene (TCB), and heated to the desireddissolution temperature (e.g. 150° C.) for 1 to 3 hours. The solution(0.5 to 1.5 ml) was then loaded into the TREF column filled withstainless steel beads. After equilibration at a given stabilizationtemperature (e.g. 110° C.) for 30 to 45 minutes, the polymer solutionwas allowed to crystallize with a temperature drop from thestabilization temperature to 30° C. (0.1 or 0.2° C./minute). Afterequilibrating at 30° C. for 30 minutes, the crystallized sample waseluted with TCB (0.5 or 0.75 mL/minute) with a temperature ramp from 30°C. to the stabilization temperature (0.25 or 1.0° C./minute). The TREFcolumn was cleaned at the end of the run for 30 minutes at thedissolution temperature. The data were processed using Polymer ChARsoftware, Excel spreadsheet and TREF software developed in-house.

The TREF procedures described above are well known to persons skilled inthe art and can be used to determine the modality of a TREF profile, aCDBI₅₀, a copolymer wt % eluting at or below 40° C., a copolymer wt %eluting at above 100° C., a copolymer wt % eluting at from 90° C. to105° C., a T(75)−T(25) value, as well as the temperatures or temperatureranges where elution intensity maxima (elution peaks) occur.

The melting points including a peak melting point (T_(m)) and thepercent crystallinity of the copolymers are determined by using a TAInstrument DSC Q1000 Thermal Analyzer at 10° C./min. In a DSCmeasurement, a heating-cooling-heating cycle from room temperature to200° C. or vice versa is applied to the polymers to minimize thethermo-mechanical history associated with them. The melting point andpercent of crystallinity are determined by the primary peak temperatureand the total area under the DSC curve respectively from the secondheating data. The peak melting temperature T_(m) is the highertemperature peak, when two peaks are present in a bimodal DSC profile(typically also having the greatest peak height).

The melt strength of a polymer is measured on Rosand RH-7 capillaryrheometer (barrel diameter=15 mm) with a flat die of 2-mm Diameter, L/Dratio 10:1 at 190° C. Pressure Transducer: 10,000 psi (68.95 MPa).Piston Speed: 5.33 mm/min. Haul-off Angle: 52°. Haul-off incrementalspeed: 50-80 m/min² or 65±15 m/min². A polymer melt is extruded througha capillary die under a constant rate and then the polymer strand isdrawn at an increasing haul-off speed until it ruptures. The maximumsteady value of the force in the plateau region of a force versus timecurve is defined as the melt strength for the polymer.

Dynamic Mechanical Analysis (DMA). Rheological measurements (e.g.small-strain (10%) oscillatory shear measurements) were carried out on adynamic Rheometrics SR5Stress rotational rheometer with 25 mm diameterparallel plates in a frequency sweep mode under full nitrogenblanketing. The polymer samples are appropriately stabilized with theanti-oxidant additives and then inserted into the test fixture for atleast one minute preheating to ensure the normal force decreasing backto zero. All DMA experiments are conducted at 10% strain, 0.05 to 100rad/s and 190° C. Orchestrator Software is used to determine theviscoelastic parameters including the storage modulus (G′), loss modulus(G″), phase angle (δ), complex modulus (G*) and complex viscosity (η*).

The complex viscosity |η*(ω)| versus frequency (ω) data were then curvefitted using the modified three parameter Carreau-Yasuda (CY) empiricalmodel to obtain the zero shear viscosity η₀, characteristic viscousrelaxation time τ_(η), and the breadth of rheology parameter-a. Thesimplified Carreau-Yasuda (CY) empirical model used is as follows:|η*(ω)|=η₀/[1+(τ_(η)ω)^(a)]^((1-n)/a)

wherein: |η*(ω)|=magnitude of complex shear viscosity; η₀=zero shearviscosity; τ_(η)=characteristic relaxation time; a=“breadth” of rheologyparameter (which is also called the “Carreau-Yasuda shear exponent” orthe “CY a-parameter” or simply the “a-parameter” in the currentinvention); n=fixes the final power law slope, fixed at 2/11; andω=angular frequency of oscillatory shearing deformation. Details of thesignificance and interpretation of the CY model and derived parametersmay be found in: C. A. Hieber and H. H. Chiang, Rheol. Acta, 28, 321(1989); C. A. Hieber and H. H. Chiang, Polym. Eng. Sci., 32, 931 (1992);and R. B. Bird, R. C. Armstrong and O. Hasseger, Dynamics of PolymericLiquids, Volume 1, Fluid Mechanics, 2nd Edition, John Wiley & Sons(1987); each of which is incorporated herein by reference in itsentirety.

The Shear Thinning Index (SHI) was determined according to the methodprovided in U.S. Pat. Appl. No. 2011/0212315: the SHI is defined asSHI(ω)=η*(ω)/η⁰ for any given frequency (ω) for dynamic viscositymeasurement, wherein η0 is zero shear viscosity @190° C. determined viathe empiric Cox-Merz-rule. η* is the complex viscosity @190° C.determinable upon dynamic (sinusoidal) shearing or deformation of acopolymer as determined on a Rheometrics SR5Stress rotational rheometerusing parallel-plate geometry. According to the Cox-Merz-Rule, when thefrequency (ω) is expressed in Radiant units, at low shear rates, thenumerical value of η* is equal to that of conventional, intrinsicviscosity based on low shear capillary measurements. The skilled personin the field of rheology is well versed with determining η⁰ in this way.The shear thinning ratio shear thinning ratio (η*_(0.1)/η*₁₀) can bedetermined similarly using DMA by determining the complex viscosity atfrequencies 0.1 and 10 rad/sec.

The films of the current examples were made on a blown film linemanufactured by Battenfeld Gloucester Engineering Company of Gloucester,Mass. using a die diameter of 4 inches, and a die gap of 35 or 100 mil.This blown film line has a standard output of more than 100 pounds perhour and is equipped with a 50 horsepower motor. Screw speed was 35 to50 RPM. The extender screw has a 2.5 mil diameter and a length/diameter(L/D) ratio of 24/1. Melt Temperature and Frost Line Height (FLH) are420 to 430° F. and 16 to 18 inches respectively. The blown film bubbleis air cooled. Typical blow up ratio (BUR) for blown films prepared onthis line are from 1.5/1 to 4/1. An annular die having a gap of 35 milswas used for these experiments. The films of this example were preparedusing a BUR aiming point of 2.5:1 and a film thickness aiming point of1.0 mils.

The haze (%) was measured in accordance with the procedures specified inASTM D 1003-07, using a BYK-Gardner Haze Meter (Model Haze-gard plus).

Dart impact strength was measured on a dart impact tester (ModelD2085AB/P) made by Kayeness Inc. in accordance with ASTM D-1709-04(method A).

Machine (MD) and transverse (TD) direction Elmendorf tear strengths weremeasured on a ProTear™ Tear Tester made by Thwing-Albert Instrument Co.in accordance with ASTM D-1922.

Puncture resistance was measured on a MTS Systems Universal Tester(Model SMT(HIGH)-500N-192) in accordance with ASTM D-5748

MD or TD secant modulus was measured on an Instrument 5-Head UniversalTester (Model TTC-102) at a crosshead speed of 0.2 in/min up to 10%strain in accordance with ASTM D-882-10. The MD or TD secant modulus wasdetermined by an initial slope of the stress-strain curve from an originto 1% strain.

Film tensile testing was conducted on an Instrument 5-Head UniversalTester (Model TTC-102) in accordance with ASTM D-882-10.

Gloss was measured on a BYK-Gardner 45° Micro-Gloss unit in accordancewith ASTM D2457-03.

A seal was prepared by clamping two 2.0 mil film strips between heatedupper and lower seal bars on a SL-5 Sealer made by Lako Tool for 0.5seconds, 40 psi seal bar clamping pressure for each temperature in therange from onset of seal to melt through. Seal strength or sealabilityparameter was measured as a function of seal temperature on anInstrument 5-Head Universal Tester (Model TTC-102) in accordance withASTM F88-09.

Polymer Blend Components

Resins 1A-1F: The First Polyethylene Copolymer.

These resins were made using a supported catalyst having the formula(1-C₆F₅CH₂-Indenyl)((t-Bu)₃P═N)TiCl₂ as is further described below.

Synthesis of (1-C₆F₅CH₂-Indenyl)((t-Bu)₃P═N)TiCl₂.

To distilled indene (15.0 g, 129 mmol) in heptane (200 mL) was addedBuLi (82 mL, 131 mmol, 1.6 M in hexanes) at room temperature. Theresulting reaction mixture was stirred overnight. The mixture wasfiltered and the filter cake washed with heptane (3×30 mL) to giveindenyllithium (15.62 g, 99% yield). Indenyllithium (6.387 g, 52.4 mmol)was added as a solid over 5 minutes to a stirred solution of C₆F₅CH₂—Br(13.65 g, 52.3 mmol) in toluene (100 mL) at room temperature. Thereaction mixture was heated to 50° C. and stirred for 4 h. The productmixture was filtered and washed with toluene (3×20 mL). The combinedfiltrates were evaporated to dryness to afford 1-C₆F₅CH₂-indene (13.58g, 88%). To a stirred slurry of TiCl₄.2THF (1.72 g, 5.15 mmol) intoluene (15 mL) was added solid (t-Bu)₃P═N—Li (1.12 g, 5 mmol) at roomtemperature. The resulting reaction mixture was heated at 100° C. for 30min and then allowed to cool to room temperature. This mixturecontaining ((t-Bu)₃P═N)TiCl₃ (1.85 g, 5 mmol) was used in the nextreaction. To a THF solution (10 mL) of 1-C₆F₅CH₂-indene (1.48 g, 5 mmol)cooled at −78° C. was added n-butyllithium (3.28 mL, 5 mmol, 1.6 M inhexanes) over 10 minutes. The resulting dark orange solution was stirredfor 20 minutes and then transferred via a double-ended needle to atoluene slurry of ((t-Bu)₃P═N)TiCl₃ (1.85 g, 5 mmol). The cooling wasremoved from the reaction mixture which was stirred for a further 30minutes. The solvents were evaporated to afford a yellow pasty residue.The solid was re-dissolved in toluene (70 mL) at 80° C. and filteredhot. The toluene was evaporated to afford pure(1-C₆F₅CH₂-Indenyl)((t-Bu)₃P═N)TiCl₂ (2.35 g, 74%).

Drying of the Catalyst Modifier.

950 g of commercially available Armostat® 1800 (mp 50° C., bp>300° C.),which was used as a catalyst modifier, was loaded in a 2 L-round bottomflask and melted in an oil bath at 80° C. The oil bath temperature wasthen raised to 110° C. and a high vacuum was applied while maintainingstirring. At first, a lot of bubbles were seen due to the release of gasand moisture vapor. Approximately two hours later, gas evolutionsubsided and heating/evacuation was continued for another hour. TheArmostat 1800 material was then cooled down to room temperature andstored under nitrogen atmosphere until use.

To determine the level of moisture in the Armostat 1800, a 15 wt % of anArmostat solution in pre-dried toluene was prepared and the moisture ofthe solution was determined by Karl-Fischer titration method. Themoisture levels in Armostat 1800 as received from the commercialsupplier, as well as that dried by traditional methods (i.e. drying thesolution over molecular sieves) and by use of low pressure waterdistillation was determined. The unpurified catalyst modifier was foundto make a 15 wt % toluene solution having 138 ppm of H₂O. The catalystmodifier which was dried over molecular sieves was found to make a 15 wt% toluene solution having 15-20 ppm of H₂O. The catalyst modifier whichwas dried by vacuum distillation of water was found to make a 15 wt %toluene solution having 14-16 ppm of H₂O. It has thus been shown, thatsimple vacuum distillation to remove water is as effective as dryingmethods which employ molecular sieves. In fact, the vacuum distillationhas an advantage over use of molecular sieves as a drying agent in thatit is far less time consuming (molecular sieves took over 2 days to drythe catalyst modifier sufficiently and multiple batches of the sieveswere needed), and more cost effective (the use of sieves led to adecrease in the concentration of the catalyst modifier in toluenesolution due to catalyst modifier absorption into the sieves, andrequired large quantities of solvent to sufficiently solubilize thecatalyst modifier in order to make efficient contact with the sieves).

Preparation of Supported Catalyst.

Sylopol 2408 silica purchased from Grace Davison was calcined byfluidizing with air at 200° C. for 2 hours and subsequently withnitrogen at 600° C. for 6 hours. 114.273 grams of the calcined silicawas added to 620 mL of toluene. 312.993 g of a MAO solution containing4.5 weight % Al purchased from Albemarle was added to the silica slurryquantitatively. The mixture was stirred for 2 hours at ambienttemperature. The stirring rate should be such so as not to break-up thesilica particles. 2.742 grams of (1-C₆F₅CH₂-Indenyl)((t-Bu)₃P═N)TiCl₂(prepared as above in Example 1) was weighed into a 500-mL Pyrex bottleand 300 mL of toluene added. The metal complex solution was added to thesilica slurry quantitatively. The resulting slurry was stirred for 2hours at ambient temperature. 21.958 g of 18.55 wt % toluene solution ofArmostat® 1800 was weighed into a small vessel and transferredquantitatively to the silica slurry. The resulting mixture was stirredfor a further 30 minutes after which the slurry was filtered, yielding aclear filtrate. The solid component was washed with toluene (2×150 mL)and then with pentane (2×150 mL). The final product was dried in vacuoto between 450 and 200 mtorr and stored under nitrogen until used. Thefinished catalyst had a pale yellow to pale orange color. The catalysthad 2.7 wt % of Armostat present.

Polymerization—TSR

Continuous ethylene/1-hexene gas phase copolymerization experiments wereconducted in a 56.4 L Technical Scale Reactor (TSR) in continuous gasphase operation (for an example of a TSR reactor set up, see Eur. Pat.Appl. No. 659,773A1). Ethylene polymerizations were run at 75° C. to 90°C. with a total operating pressure of 300 pounds per square inch gauge(psig). Gas phase compositions for ethylene and 1-hexene were controlledvia closed-loop process control to values of 65.0 and 0.5-2.0 mole %,respectively. Hydrogen was metered into the reactor in a molar feedratio of 0.0008-0.0020 relative to ethylene feed during polymerization.Nitrogen constituted the remainder of the gas phase mixture(approximately 34-64 mole %). A typical production rate for theseconditions is 2.0 to 3.0 kg of polyethylene per hour. A seed-bed wasused and prior to polymerization start-up was washed with a small amountof triethylaluminum, TEAL to scavenge impurities. Prior to introductionof the catalyst TEAL was flushed from the reactor. The catalyst was fedto the reactor together with small amount of dilute TEAL solution (0.25wt %) during the start-up phase. The addition of TEAL was discontinuedonce the desired polymer production rate was reached. Alternatively, thereactor can be started with the catalyst feed line alone during thepolymerization start-up phase (that is, without initially feeding theTEAL solution). The polymerization reaction was initiated underconditions of low comonomer concentration, followed by gradualadjustment of the comonomer to ethylene ratio to provide the targetedpolymer density.

Pelletization of Granular Resins.

500 ppm of Irganox 1076 and 1000 ppm of Irgafos 168 were dry blendedwith the granular resin prior to pelletization. The resulting powderblend was extruded on Leistritz twin-screw extruder with a screwdiameter of 38 mm and L/D ratio of 33/1 under nitrogen atmosphere tominimize polymer degradation. The pelletization conditions of theextruder were set at a melt temperature of 210° C. an output rate of 20to 25 lb/hr, a screw speed of 120 rpm and a pelletizer speed of 30 to 40rpm. The pelleted resin was cooled and then collected for the resincharacterization and film evaluation.

Catalyst composition information and steady state polymerizationconditions are provided in Table 1 for examples 1A and 1B (C2=ethylene;C6=1-hexene; H2=hydrogen; and C6/C2 for example is the molar feed ratioof each component to the reactor). Polymer data for the resulting resins1A and 1B are provided in Table 2.

Polymerization-Pilot Plant

Ethylene/1-hexene copolymerization experiments were conducted in acontinuous fluidized bed gas phase Pilot Plant scale reactor. An exampleof a reactor configuration and typical process operational parameters isgiven in, for example, U.S. Pat. No. 8,338,551 B2 and in Eur. Pat. Appl.No. 1,308,464 A1 (see Examples 10 and 11). Ethylene polymerizations wererun at 80° C. to 85° C. with a total operating pressure of 300 poundsper square inch gauge (psig). Gas phase compositions for ethylene and1-hexene were controlled via closed-loop process control to values of35-50.0 and 0.5-2.0 mole %, respectively. Hydrogen was metered into thereactor in a molar feed ratio of 0.0008-0.0015 relative to ethylene feedduring polymerization. Nitrogen constituted the remainder of the gasphase mixture (approximately 34-49 mole %). A typical production ratefor these conditions is 100 to 250 kg of polyethylene per hour. Aseed-bed was used and prior to polymerization start-up was washed with asmall amount of triethylaluminum, TEAL to scavenge impurities. Therequired gas composition of ethylene, 1-hexene, hydrogen, nitrogen andpentane/isopentane in the reactor is built to target amounts beforeinjection of catalyst. The level of pentane/isopentane can range from 9to 17 mole % in the reactor. The reactor was started with the catalystfeed line alone without additional scavenging with TEAL during thepolymerization start-up. The polymerization reaction was initiated underconditions of lower comonomer concentration and higher hydrogenconcentration, followed by gradual adjustment of the comonomer toethylene ratio and hydrogen to ethylene ratio to achieve targetedpolymer density and melt index. Pelletization of the granular resin wascarried out as per TSR scale (see above).

Catalyst composition information and steady state polymerizationconditions are provided in Table 1 for examples 1C-1F (C2=ethylene;C6=1-hexene; H2=hydrogen; and C6/C2, for example, is the molar feedratio of each component to the reactor). Polymer data for the resultingresins 1C-1F are provided in Table 2.

TABLE 1 TSR Pilot Plant Example No. 1A 1B 1C 1D 1E IF Catalyst Ti, wt %0.14 0.12 0.12 0.134 0.134 0.134 Al, wt % 9.4 7 7 7.86 7.86 7.86 Si, wt% 35.5 38.3 37.8 37.3 37.3 37.3 Armostat, wt % 2.7 2.5 2.5 2.5 2.5 2.5Process Productivity (g PE/g Cat) 3400 1300 2480 3675 5656 5339 Ethylene(mole %) 50 56 39 45 46 44 Hydrogen (mol %) 0.035 0.034 0.029 0.0270.032 0.032 1-Hexene (mol %) 0.8603 0.9586 0.6903 0.8562 0.8049 0.7671C6/C2 (mol/mol feed to reactor) 0.0232 0.0215 0.0251 0.0260 0.02600.0260 H2/C2 (mol/mol feed to reactor) 0.0013 0.0013 0.0015 0.00150.0019 0.0019 H2/C2 in reactor (mol/mol Gas 0.00070 0.00062 0.000750.00060 0.00070 0.00073 composition) C6/C2 in reactor (mol/mol Gas0.0172 0.0173 0.0176 0.0190 0.0175 0.0175 composition) Temp (° C.) 80 8082.5 82.5 80.0 82.5 Production rate (kg/hr) 2.58 2.46 180 172 202 202Residence Time (hrs) 1.8 1.8 2.6 2.0 2.4 2.5 Bulk Density (lb per cubicfoot) 22.5 19.5 20.6 24.5 28.2 26.1 Isopentane and Pentane in 0 11 17 1112 11 reactor, (mole %) TEAL as scavenger yes no no no no No

TABLE 2 Copolymer Properties Copolymer No. 1A 1B 1C 1D 1E 1F density(g/cc) 0.9208 0.922 0.922 0.9214 0.9224 0.9228 MI, I₂ (g/10 min) 0.580.53 0.52 0.57 0.56 1.22 MFR, I₂₁/I₂ 44.5 42.7 33.5 37.8 43 35.3 I₁₀/I₂10.9 10.6 9.11 9.67 10.3 9.1 Comonomer 1-hexene 1-hexene 1-hexene1-hexene 1-hexene 1-hexene TREF profile trimodal, multimodal, multimodalmultimodal, multimodal, multimodal, T(low) = T(high) = T(low) = T(high)= T(high) = T(high) = 71.5° C.; 93.6° C.; 77.7° C. 93.1° C.; 93.2° C.;93.1° C.; T(med) = T(low) = T(high) = T(low) = T(low) = T(low) = 81.3°C.; 73.6° C. 93.4° C. 73.4° C. 74.4° C. 74.9° C. T(high) = 92.3° C.T(med)-T(low), ° C. 9.8 — NA — — — T(high)-T(med), ° C. 11.0 — NA — — —T(high)-T(low), ° C. 20.8 20.0 15.7 19.7 18.8 18.2 wt % at 90-105° C.12.9 15.4 15.4 15.1 14.6 13.9 T(75)-T(25) (° C.) 14.4 13.75 9.7 13.713.3 13 CDBI₅₀ (wt %) 65.6 64.1 70.8 64.2 65.1 64.9 comonomer profilereverse reverse reverse reverse reverse Reverse DSC melt temp (° C.)104.2, 106.4, 109.1, 107.2, 106.6, 108.5, 120.3 121.1 120.4 120.9 120.7120.5 % crystallinity 46.1 46.8 49.3 46.6 48.3 48.7 CY a-parameter0.0947 0.1228 0.1962 0.2622 0.2320 0.2221 M_(n) 20.3 × 10³ 24228 2659425646 20438 20022 M_(w) 97.3 × 10³ 120830 119814 126052 121308 103207M_(z) 226.4 × 10³  355544 319542 374146 359545 313009 M_(w)/M_(n) 4.784.99 4.51 4.92 5.94 5.15 M_(z)/M_(w) 2.33 2.94 2.67 2.97 2.96 3.03 C₆content (wt %) 7.3 6.8 6.0 6.8 6.8 6.5 SCB/1000 C 12.7 11.8 10.5 11.811.9 11.3 hexane extractables (%) 0.94 0.89 0.60 0.80 0.90 0.90 meltstrength (cN) 5.74 6.39 6.41 6.27 6.00 3.81 VGP crossover phase angle59.6 62.81 66.49 64.74 62.01 67.43 (δ^(XO)) SCB/1000 C at MW of 200,000-6.1 6.6 3.7 5.9 5.9 5.3 SCB/1000 C at MW of 50,000 Shear Thinning Index(SHI) 0.015 0.123 0.303 0.459 0.343 0.429 83.0-1.25(CDBI₅₀)/(M_(w)/M_(n)) 65.85 66.94 63.37 66.69 69.30 67.2580.7-(CDBI₅₀)/(M_(w)/M_(n)) 66.98 67.85 65.0 67.65 69.74 68.10 72[(I₂₁/I₂)⁻¹ + 10⁻⁶ (M_(n))] 3.08 3.43 4.06 3.75 3.15 3.48

Resin 2A: The Second Polyethylene Copolymer.

This resin was made using a supported catalyst having the formula(1,2-(n-propyl)(C₆F₅)Cp)Ti(N═P(t-Bu)₃)Cl₂ as is further described below.

Preparation of the Supported Catalyst.

To a slurry of dehydrated silica (122.42 g) in toluene (490 mL) wasadded a 10 wt % MAO solution (233.84 g of 4.5 wt % Al in toluene) over10 minutes. The vessel containing the MAO was rinsed with toluene (2×10mL) and added to the reaction mixture. The resultant slurry was stirredwith an overhead stirrer assembly (200 rpm) for 1 hour at ambienttemperature. To this slurry was added a toluene (46 mL) solution of(1,2-(n-propyl)(C₆F₅)Cp)Ti(N═P(t-Bu)₃)Cl₂ (2.28 g) over 10 minutes. Thissolution may need to be gently heated to 45° C. for a brief period (5minutes) to fully dissolve the molecule. The vessel containing themolecule was rinsed with toluene (2×10 mL) and added to the reactionmixture. After stirring for 2 hours (200 rpm) at ambient temperature atoluene (22 mL) solution of Armostat-1800 (which was previously driedaccording to the method above for “Drying a Catalyst Modifier”) at 8.55wt % was added to the slurry which was further stirred for 30 minutes.The slurry was filtered and rinsed with toluene (2×100 mL) and then withpentane (2×100 mL). The catalyst was dried in vacuo to less than 1.5 wt% residual volatiles. The solid catalyst was isolated and stored undernitrogen until further use. The catalyst had 2.7 wt % of Armostatpresent.

Polymerization

Continuous ethylene/1-hexene gas phase copolymerization experiments wereconducted in a 56.4 L Technical Scale Reactor (TSR) in continuous gasphase operation. Ethylene polymerizations were run at 75° C. to 90° C.with a total operating pressure of 300 pounds per square inch gauge(psig). Gas phase compositions for ethylene and 1-hexene were controlledvia closed-loop process control to values of 65.0 and 0.5-2.0 mole %,respectively. Hydrogen was metered into the reactor in a molar feedratio of 0.0008-0.0015 relative to ethylene feed during polymerization.Nitrogen constituted the remainder of the gas phase mixture(approximately 38 mole %). A typical production rate for theseconditions is 2.0 to 3.0 kg of polyethylene per hour.

Pelletization of Granular Resins.

500 ppm of Irganox 1076 and 1000 ppm of Irgafos 168 were dry blendedwith the granular resin prior to pelletization. The resulting powderblend was extruded on Leistritz twin-screw extruder with a screwdiameter of 38 mm and L/D ratio of 33/1 under nitrogen atmosphere tominimize polymer degradation. The pelletization conditions of theextruder were set at a melt temperature of 210° C. an output rate of 20to 25 lb/hr, a screw speed of 120 rpm and a pelletizer speed of 30 to 40rpm. The pelleted resin was cooled and then collected for the resincharacterization and film evaluation.

Steady state polymerization conditions are provided in Table 3(C2=ethylene; C6=1-hexene; C6/C2 is the molar feed ratio of eachcomponent to the reactor) for example 2A. Polymer data for the resulting2A resin is provided in Table 4.

TABLE 3 Catalyst Comp. 2A Productivity (g PE/g Cat) 7700 Hydrogen (mol%) 0.0298 1-Hexene (mol %) 1.2110 C6/C2 (mol/mol feed) 0.0215 Temp (°C.) 85 Production rate (kg/hr) 2.53 Residence Time (hrs) 1.62 BulkDensity (lb per cubic foot) 17.9 Isopentane (weight %) 0

Also included in Table 4 are resins, 2B, 2B*, 2C, and 2D each of whichmay be used as the second polyethylene copolymer in the blends of thecurrent invention. Resin 2B is an Exceed 1018DA™ ethylene copolymer of1-hexene, which is commercially available from ExxonMobil. Resin 2B* isan Exceed 1018JA™ ethylene copolymer of 1-hexene, which is commerciallyavailable from ExxonMobil. Resin 2C is a linear low density polyethylenehaving a melt index I₂ of 0.93 g/10 min and a density of 0.917 g/cm³which is available from NOVA Chemicals as FPs-1,7-C™. Resin 2D is alinear low density polyethylene having a melt index I₂ of 1 g/10 min anda density of 0.92 g/cm³, which is available from NOVA Chemicals asFP-120-C™.

TABLE 4 Copolymer Properties Resin No. 2A 2B 2B* 2C 2D density (g/cm³)0.9173 0.9212 0.9216 0.9168 0.9198 MI, I₂ (g/10 min) 0.95 0.97 0.96 0.931.04 MFR, I₂₁/I₂ 15.5 16.0 15.9 30.1 29.0 I₁₀/I₂ 5.61 5.65 5.70 7.52 8.0Comonomer 1-hexene 1-hexene 1-hexene 1-octene 1-octene TREF profilebimodal bimodal bimodal, bimodal bimodal T(low) = T(low) = T(high) =T(low) = T(low) = 81.0° C. T(high) = 83.3° C. T(high) = 93.7° C. T(low)= 78.5° C. 81.1° C. 91.8° C. 93.0° C. 83.5° C. T(high) = T(high) = 94.7°C. 95.4° C. T(med)-T(low), ° C. NA NA NA NA NA T(high)-T(med), ° C. NANA NA NA NA T(high)-T(low), ° C. 10.8 9.7 10.2 16.2 14.3 wt % at 90-105°C. 9.7 7.9% 10.3 5.6 15.9 T(75)-T(25) (° C.) 9.7 10.6 10.1 8.25 14.4CDBI₅₀ (wt %) 74.5 70.5 71.1 74.5 58.1 comonomer profile flat slightlyreverse slightly negative negative reverse DSC melt temp (° C.) 109.5,119.6 110.8, 118.9 109.7, 118.7 108.2, 112.3 109.4, 119.6 %crystallinity 44.3 43.0 45.7 42.5 44.5 CY a-parameter 0.642 0.733 0.72990.593 0.402 M_(w) (×10⁻³) 98.3 103.3 110.4 96.6 103.4 M_(n) (×10⁻³) 56.646.0 52.1 29.3 28.9 M_(z) (×10⁻³) 154.6 174.1 195.8 229.4 298.9M_(w)/M_(n) 1.74 2.25 2.12 3.30 3.58 M_(z)/M_(w) 1.57 1.69 1.77 2.382.89 comonomer content (wt %) 6.0 6.0 6.2 10.4 9.2 SCB/1000 C. 10.5 10.410.7 14.1 12.3 hexane extractables (%) 0.15 0.34 0.27 0.42 0.54 meltstrength (cN) 3.07 2.60 2.5 2.48 3.24 VGP crossover phase angle (δ^(XO))84.5 84.8 84.8 78.5 74.6 SCB/1000 at MW of 200,000-SCB/1000 at 0.6 1.21.6 −2.0 −0.6 MW of 50,000 Shear Thinning Index (SHI) 0.98 0.99 0.9850.94 0.81 83.0-1.25 (CDBI₅₀)/(M_(w)/M_(n)) 29.48 43.8 41.08 54.78 62.7180.7-(CDBI₅₀)/(M_(w)/M_(n)) 37.98 49.37 47.16 58.12 64.47 72[(I₂₁/I₂)⁻¹ + 10⁻⁶ (M_(n))] 8.72 7.812 8.28 4.50 4.56

As shown in Tables 2 and 4, the first polyethylene copolymers, resins1A-1F have a melt flow ratio that is distinct from resins 2A-2D. Theresins 1A-1F have a MFR (I₂₁/I₂) of greater than 32, while the resins2A, 2B and 2B* each have a melt flow ratio of less than 16.5 and resins2C and 2D have an MFR (I₂₁/I₂) close to 30.

As can be seen in Table 2 all the resins 1A-1E have a reverse comonomerdistribution, a multimodal TREF profile, a CDBI₅₀ within a range of from45 wt % to 75 wt %, a MFR (I₂₁/I₂) within a range of 32 to 50, aM_(w)/M_(n) within a range of from 3.5 to 6.0 and a fractional meltindex (I₂ of less than 1.0 g/10 min). Also shown in Table 2 is resin 1Fwhich has a reverse comonomer distribution, a multimodal TREF profile, aCDBI₅₀ within a range of from 45 wt % to 75 wt %, a MFR (I₂₁/I₂) withina range of 32 to 50, a M_(w)/M_(n) within a range of from 3.5 to 6.0 anda melt index I₂ of about 1.2 g/10 min. Each of the resins 1A-1F shown inTable 2, have a broad unimodal molecular weight distribution.

A representative TREF curve is shown in FIG. 1A for resin 1A. Arepresentative TREF curve is shown in FIG. 1B for resin 1B. Arepresentative GPC curve is shown for resin 1A in FIG. 2. Arepresentative GPC-FTIR curve is shown for resin 1A in FIG. 3.

A Van Gurp-Palmen analysis is a means by which to study a polymerarchitecture (e.g., molecular weight distribution, linearity, etc.) asreflected by the polymer melt morphology. A VGP curve is simply a plotof the phase angle (δ) versus complex modulus (G*), where the tworheology parameters are obtained using the frequency sweep test indynamic mechanical analysis (DMA). A shift of a VGP curve from abaseline curve or a decrease in the phase angles at the mid-range ofcomplex modulus may indicate changes in the polymer melt morphology.

A VGP plot allows for a determination of the crossover rheologyparameter which is defined as the intersecting point obtained betweenthe phase angle (δ) vs. complex modulus (G*) plot and a phase angle (δ)vs. complex viscosity (η*) plot. Based on a linear viscoelasticitytheory, the VGP crossover rheology parameter or “crossover phase angle”(δ^(XO)) occurs at a frequency (ω) which is equal to unity. It is thephase angle at which the numerical values of G* and the η* areequivalent. Hence the VGP crossover rheology parameter can be determinedin a single DMA test.

The VGP crossover plots for resin 2A and for a resin sold under thetrade-name Exceed 1018DA™ (resin 2B) are included in FIG. 4A. The VGPcrossover plots for the resin 1A are shown in FIG. 4B. The VGP crossoverpoints are dependent upon the copolymer architecture. Generally, forresins which are easier to process such as resin 1A, the VGP phase angleat which crossover occurs defined as δ^(XO) is lower than for resinswhich are more difficult to process such as resins 2A and 2B (compareFIGS. 4A and 4B). Without wishing to be bound by any single theory, thismay be due to the fact that resin 1A has greater melt flow ratio (I₂₁/₂)or a broader molecular weight distribution (M_(w)/M_(n)) than Resin 2Aor 2B. For resins that are easier to process, the shape of the phaseangle-complex viscosity curves and the shape of the phase-angle complexmodulus curves, are deflected somewhat and more closely resemble mirrorimages of each other, relative to the curves obtained for resins whichare more difficult to process (compare the curves in FIG. 4A with thecurves in FIG. 4B).

As shown in Tables 2, the first polyethylene copolymers, resins 1A-1Fhave a δ^(XO) value that is less than about 70°. In fact resins 1A-1Fhave a δ^(XO) value that is between about 55° and about 70°.

Also shown in Table 2, is the fact that all of the ethylene copolymers1A-1F satisfy the following relationships: (M_(w)/M_(n))≧72[(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))] where M_(w), M_(n), I₂₁, I₂ and CDBI₅₀ are allas defined as above. Resins 1A, 1B and 1D-1F also satisfy the followingrelationship: δ^(XO)≦80.7−(CDBI₅₀)/(M_(w)/M_(n)) at a δ^(XO) of 55° to70°, where δ^(XO) is the crossover phase angle, M_(w), M_(n), I₂₁, I₂and CDBI₅₀ are all as defined as above. Resins 1A, 1B, 1D, and 1E alsosatisfy the following relationship: δ^(XO)≦83.0−1.25(CDBI₅₀)/(M_(w)/M_(n)), where δ^(XO) is the crossover phase angle,M_(w), M_(n), I₂₁, I₂ and CDBI₅₀ are all as defined as above. Incontrast, the data provided in Table 4, shows that none of the resins2A-2D satisfy any of the conditions: (M_(w)/M_(n))≧72 [(I₂₁/I₂)⁻¹+10⁻⁶(M_(n))]; (δ^(XO)≦83.0−1.25 (CDBI₅₀)/(M_(w)/M_(n)); orδ^(XO)≦80.7−(CDBI₅₀)/(M_(w)/M_(n)) at δ^(XO) of 55° to 70°.

For further comparison purposes, ethylene copolymers 1A-1F have beenplotted against several known commercial resins in FIG. 5. FIG. 5 showsa plot of the equation: (M_(w)/M_(n))=72 [(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))], aswell as a plot of the Mw/Mn vs. 72 [(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))] values forresins 1A-1F as well as several known commercial resins. The commercialresins included in FIG. 5 for comparison purposes are all resins havingan melt index I₂ of 1.5 g/10 min or less and a density of between 0.916and 0.930 g/cm³ and which are sold under trade names such as, Elite™,Exceed™ Marflex™, Starflex™, Dowlex™, SURPASS™, SCLAIR™, NOVAPOL™ andEnable™. As can be seen from FIG. 5, none of these commercial gradessatisfy the condition: (M_(w)/M_(n))≧72 [(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))]. Incontrast, all of the resins 1A-1F satisfy the condition:(M_(w)/M_(n))≧72 [(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))]. This work demonstrates thedistinct architecture of the resins used as the first polyethylenecopolymer in the blends of the current invention.

For further comparison purposes, ethylene copolymers 1A-1F have beenplotted against several known commercial resins in FIG. 6. FIG. 6 showsa plot of the equation: δ^(XO)=83.0−1.25 (CDBI₅₀)/(M_(w)/M_(n)), as wellas a plot of the δ^(XO) vs. 83.0−1.25 (CDBI₅₀)/(M_(w)/M_(n)) values forresins 1A-1F and several known commercial resins. The commercial resinsincluded in FIG. 6 for comparison purposes are all resins having a meltindex I₂ of 1.5 g/10 min or less and a density of between 0.916 and0.930 g/cm³ and which are sold under trade names such as, Elite™,Exceed™, Marflex™, Starflex™, Dowlex™, SURPASS™, SCLAIR™, NOVAPOL™ andEnable™. As can be seen from the figure, none of these commercial gradessatisfy the condition: δ^(XO)≦83.0−1.25 (CDBI₅₀)/(M_(w)/M_(n)). Incontrast, resins 1A, 1B, 1D, and 1E satisfy the condition:δ^(XO)≦83.0−1.25 (CDBI₅₀)/(M_(w)/M_(n)). This work further demonstratesthe distinct architecture of the resins used as the first polyethylenecopolymer in the blends of the current invention.

For further comparison purposes, ethylene copolymers 1A-1F have beenplotted against several known commercial resins in FIG. 7. FIG. 7 showsa plot of the equation: δ^(XO)=80.7−(CDBI₅₀)/(M_(w)/M_(n)), as well as aplot of the δ^(XO) vs. 80.7−(CDBI₅₀)/(M_(w)/M_(n)) values for resins1A-1F and several known commercial resins. FIG. 7 also shows which ofthe resins 1A-1F and which of the commercial resins have a δ^(XO) offrom 55° to 70°. The commercial resins included in FIG. 7 for comparisonpurposes are all resins having an melt index I₂ of 1.5 g/10 min or lessand a density of between 0.916 and 0.930 g/cm³ and which are sold undertrade names such as, Elite™, Exceed™, Marflex™, Starflex™, Dowlex™,SURPASS™, SCLAIR™, NOVAPOL™ and Enable™. As can be seen from FIG. 7,none of these commercial grades satisfy the condition whereδ^(XO)=80.7−(CDBI₅₀)/(M_(w)/M_(n)) at a δ^(XO) of from 55° to 70°. Incontrast the resins 1A, 1B and 1D-1F satisfy the condition whereδ^(XO)=80.7−(CDBI₅₀)/(M_(w)/M_(n)) at a δ^(XO) of from 55° to 70°. Thiswork further demonstrates the distinct architecture of the resins usedas the first polyethylene copolymer in the blends of the currentinvention.

Polymer Blends

Inventive polymer blends were made by blending a first polyethylenecopolymer (e.g., resins 1A or 1C) with a second polyethylene copolymer(e.g., resins 2A-2D). The blends were made by dry blending thecomponents in appropriate amounts using a metering device upstream of anextruder used to feed a blown film line. Tables 5-8 show the filmproperties of 1 mil (thickness) films comprising 100 wt % first orsecond polyethylene copolymers as well as the film properties for 15 wt%:85 wt % polymer blends.

Comparative polymer blends were made by blending LF-Y819-A™ (a highpressure low density polyethylene (HPLDPE) material having a melt indexI₂ of 0.75 g/10 min and a density of 0.919 g/cm³, available from NOVAChemicals) with the second polyethylene copolymer (e.g. resins 2B, 2Cand 2D). The film properties of these 15 wt %:85 wt % comparative blendsare provided in Tables 6-8.

TABLE 5 Film Properties (Resin 1A, 2A and Inventive Blend of 1A/2A)First Polyethylene Second Polyethylene Inventive Copolymer CopolymerBlend 1A 100% 2A 100% 15 wt % 1A/85% wt % 2A Dart Impact (g/mil) 638 508686 MD Tear (g/mil) 121 244 200 TD Tear (g/mil) 455 330 415 Puncture(J/mm) 53 68 63 1% MD Secant Modulus (MPa) 198 153 160 1% TD SecantModulus (MPa) 220 173 174 2% MD Secant Modulus (MPa) 180 139 141 2% TDSecant Modulus (MPa) 194 148 147 MD Tensile Strength (MPa) 51.0 58.959.9 TD Tensile Strength (MPa) 48.8 50.4 56.5 MD Elongation at Break (%)477 568 570 TD Elongation at Break (%) 696 675 744 MD Yield Strength(MPa) 10.9 9.5 9.3 TD Yield Strength (MPa) 11.2 9.9 9.7 MD Elongation atYield (%) 14 14 14 TD Elongation at Yield (%) 15 19 15 Haze (%) 11.2 7.44.7 Gloss (%) 50 63 75 Cold Seal Strength: SIT (° C.) 112 103 108Maximum Force (N) 14.3 10.9 12.3 Temperature at Max. Force (° C.) 130150 140 Extruder Pressure (psi) 3450-3495 5275-5315 4805-4840 SpecificOutput Rate (lb/hr/rpm) 2.50 1.89 2.38 Specific Power (lb/hr/Amp) 2.782.13 2.22 Specific Energy (W/lb/hr) 68.4 117.5 92.7

TABLE 6 Film Properties (Resin 1A, 1C, 2B, 2B*, Inventive Blends 1A/2B,1C/2B* and Comparative Blend HPLDPE/2B) First Second ComparativePolyethylene Polyethylene Inventive Blend Copolymer Copolymer Blend 15wt % LF- 1A 1C 2B 2B* 15 wt % 1A/ 15 wt % 1C/ Y819-A/85 wt 100% 100%100% 100% 85 wt % 2B 85 wt % 2B* % 2B Dart Impact (g/mil) 638 707 707709 743 485 224 MD Tear (g/mil) 121 90 235 224 222 217 106 TD Tear(g/mil) 455 438 370 364 439 400 652 Puncture (J/mm) 53 47 37 32 43 37 271% MD Secant Modulus 198 233 144 155 163 172 170 (MPa) 1% TD SecantModulus 220 258 176 171 168 177 216 (MPa) 2% MD Secant Modulus 180 209131 138 146 156 156 (MPa) 2% TD Secant Modulus 194 220 149 146 145 160189 (MPa) MD Tensile Strength (MPa) 51.0 59.7 57.3 52.5 48 57.2 41.8 TDTensile Strength (MPa) 48.8 52.9 40.7 43.4 44.9 51.6 36.5 MD Elongationat Break (%) 477 518 574 561 552 537 536 TD Elongation at Break (%) 696696 658 669 661 675 665 MD Yield Strength (MPa) 10.9 12.1 8.9 9.6 9.810.7 10.8 TD Yield Strength (MPa) 11.2 12.3 9.4 9.5 10.5 10.6 10.3 MDElongation at Yield (%) 14 13 13 14 14 14 19 TD Elongation at Yield (%)15 14 16 15 17 14 12 Haze (%) 11.2 13.3 13.6 19.7 8.9 8.7 4.7 Gloss (%)50 43.1 46 24 63 65.5 78 Cold Seal Strength: SIT (° C.) 112 116 108 105108 112.2 107 Maximum Force (N) 14.3 15.8 10.9 10.7 12.3 10 15.5Temperature at Max. Force 130 150 150 140 160 130 150 (° C.) ExtruderPressure (psi) 3450-3495 3890-3940 4815-4850 4815-4875 5355-53904800-4845 4720-4765 Specific Output Rate 2.50 2.56 2.78 2.70 2.70 2.702.56 (lb/hr/rpm) Specific Power (lb/hr/Amp) 2.28 2.63 2.04 2.04 2.002.08 2.27 Specific Energy (W/lb/hr) 68.4 70.3 86.2 88.2 91.5 86.9 83.2

TABLE 7 Film Properties (Resin 1A, 1C, 2C, Inventive Blends 1A/2C, 1C/2Cand Comparative Blend HPLDPE/2C) First Second Polyethylene PolyethyleneInventive Comparative Copolymer Copolymer Blends Blend 1A 1C 2C 15 wt %1A/ 15 wt % 1C/ 15 wt % LF-Y819- 100% 100% 100% 85 wt % 2C 85 wt % 2CA/85 wt % 2C Dart Impact (g/mil) 638 707 435 392 304 296 MD Tear (g/mil)121 90 326 269 263 129 TD Tear (g/mil) 455 438 475 525 403 645 Puncture(J/mm) 53 47 84 87 67 59 1% MD Secant Modulus (MPa) 198 233 136 141 159158 1% TD Secant Modulus (MPa) 220 258 144 159 169 201 2% MD SecantModulus (MPa) 180 209 122 126 143 143 2% TD Secant Modulus (MPa) 194 220126 138 148 173 MD Tensile Strength (MPa) 51.0 59.7 57.6 55.1 51.4 45.2TD Tensile Strength (MPa) 48.8 52.9 52.1 47.8 46.5 42.6 MD Elongation atBreak (%) 477 518 580 563 491 530 TD Elongation at Break (%) 696 696 811780 729 839 MD Yield Strength (MPa) 10.9 12.1 8.6 9.1 10.2 9.8 TD YieldStrength (MPa) 11.2 12.3 8.9 9.2 10.1 9.1 MD Elongation at Yield (%) 1413 13 14 14 15 TD Elongation at Yield (%) 15 14 20 16 15 12 Haze (%)11.2 13.3 10.3 5.9 7.1 3.9 Gloss (%) 50 43.1 48 70 66 78 Cold SealStrength: SIT (° C.) 112 116 100 102 109 101 Maximum Force (N) 14.3 15.811.5 12.4 11.5 14.6 Temperature at Max. Force (° C.) 130 150 130 160 150150 Extruder Pressure (psi) 3450-3495 3890-3940 4005-4045 4030-40653875-3910 3540-3590 Specific Output Rate (lb/hr/rpm) 2.50 2.56 2.38 2.382.44 2.27 Specific Power (lb/hr/Amp) 2.28 2.63 2.50 2.56 2.56 2.86Specific Energy (W/lb/hr) 68.4 70.3 78.8 76.8 76.8 72.5

TABLE 8 Film Properties (Resin 1A, 1C, 2D, Inventive Blend of 1A/2D,1C/2D and Comparative Blend HPLDPE/2D) First Second ComparativePolyethylene Polyethylene Inventive Blend Copolymer Copolymer Blends 15wt % LF- 1A 1C 2D 15 wt % 1A/ 15 wt % 1C/ Y819-A/85 wt 100% 100% 100% 85wt % 2D 85 wt % 2D % 2D Dart Impact (g/mil) 638 707 223 258 263 170 MDTear (g/mil) 121 90 350 266 268 120 TD Tear (g/mil) 455 438 584 599 617682 Puncture (J/mm) 53 47 73 75 71 51 1% MD Secant Modulus 198 233 158169 171 208 (MPa) 1% TD Secant Modulus 220 258 202 193 205 238 (MPa) 2%MD Secant Modulus 180 209 146 151 159 184 (MPa) 2% TD Secant Modulus 194220 169 162 181 204 (MPa) MD Tensile Strength (MPa) 51.0 59.7 55.5 49.059.1 52.3 TD Tensile Strength (MPa) 48.8 52.9 41.5 44.3 47.8 44.0 MDElongation at Break (%) 477 518 524 553 555 564 TD Elongation at Break(%) 696 696 748 760 751 852 MD Yield Strength (MPa) 10.9 12.1 10.3 9.911 10.5 TD Yield Strength (MPa) 11.2 12.3 10.6 10.5 11.6 10.6 MDElongation at Yield (%) 14 13 13 14 14 13 TD Elongation at Yield (%) 1514 14 16 17 12 Haze (%) 11.2 13.3 8.3 8.1 8.1 4.3 Gloss (%) 50 43.1 6263 62 77 Cold Seal Strength: SIT (° C.) 112 116 108 108 112 107 MaximumForce (N) 14.3 15.8 9.4 13.6 12.8 15.3 Temperature at Max. Force 130 150125 150 150 150 (° C.) Extruder Pressure (psi) 3450-3495 3890-39403820-3870 4050-4095 3655-3700 3570-3605 Specific Output Rate 2.50 2.562.50 2.44 2.50 2.33 (lb/hr/rpm) Specific Power (lb/hr/Amp) 2.28 2.632.50 2.50 2.63 2.86 Specific Energy (W/lb/hr) 68.4 70.3 76.0 78.0 72.270.7

As shown in Table 5, a blend of resin 1A and resin 2A (a linear lowdensity polyethylene with relatively low MFR (I₂₁/I₂) and having anarrow MWD (M_(w)/M_(n)) and a melt index I₂ of 0.95 g/10 min) in a15/85 weight percent ratio has improved dart impact relative to eitherof the blend components. The blend also has a TD tear value which ismore than 10% higher than the weighted average of the blend components.That is, the so called “Rule of Mixing” indicates a positive synergisticeffect on the TD tear property in the blend (note: without wishing to bebound by any single theory, the rule of mixing indicates a positivesynergism where a blend property is better than expected based on theweighted average of the blend components; negative synergism where ablend property is worse than expected based on the weighted average ofthe blend components; the rule of mixing is followed where a blendproperty is approximately what a person skilled in the art would expectbased on the weighted average of the blend components). In addition, theblend has a haze of 4.7% and a gloss at 45° of 75, each of which issignificantly improved over either of the blend components. Finally, theMD tear, and the MD and TD 1% secant modulus, which either approximatelyfollow the Rule of Mixing or are at least comparable to that of resin2A, are not impacted in a negative way. The blend of 1A with 2A can beextruded with a specific output of 2.38 lb/hour/rpm at an extruder headpressure of from about 4800 to 4840 psi, suggesting an improvement offilm processing over resin 2A.

With reference to Table 6, a blend of resin 1A and resin 2B (a linearlow density polyethylene having a relatively low MFR (I₂₁/I₂) and havinga narrow MWD (M_(w)/M_(n)) and a melt index I₂ of about 1.0 g/10 min) ina 15/85 weight percent ratio demonstrates the synergies in the filmproperties of the blend. The blend has dart impact and punctureresistance values which are greater than weighted average of the blendcomponents, a TD tear which increases more than 10% over the weightedaverage of the blend components, and haze and gloss values which improveto levels beyond that expected for the weighted average of the blendcomponents. Further, when compared to a blend containing HPLDPE (e.g.LF-Y819-A) in the same amount as the first polyethylene copolymer 1A,film made from the inventive blend comprising 15 wt % 1A and 85 wt % 2Bhas better MD tear, dart impact and puncture resistance properties.Although a blend of resin 1C and resin 2B* (a linear low densitypolyethylene having a relatively low MFR (I₂₁/I₂) and having a narrowMWD (M_(w)/M_(n)) and a melt index I₂ of about 1.0 g/10 min) in a 15/85weight percent ratio, has a depreciated dart impact, the MD and TD tearsare greater than the weighted average of the blend components. The blendalso demonstrates synergistic improvements in the haze and gloss (i.e.,the haze and gloss values improve to well beyond the expected weightedaverage). Further, when compared to a blend containing HPLDPE (e.g.,LF-Y819-A) in the same amount as the first polyethylene copolymer 1C,film made from the inventive blend comprising 15 wt % 1C and 85 wt % 2B*has better MD tear, dart impact and puncture resistance properties. Theblends of 1A with 2B or 1C with 2B* can be extruded with a specificoutput of 2.7 lb/hour/rpm at an extruder head pressure of from 5355-5390psi or 4800-4845 psi respectively, which is at least comparable to theblend comprising equivalent amounts of HPLDPE.

With reference to Table 7, a blend of resin 1A with 2C (a linear lowdensity polyethylene having a melt index I₂ of 0.93 g/10 min and adensity of 0.917 g/cm³) in a 15/85 weight percent ratio has TD tear,puncture resistance, haze and gloss values which are all improved beyondthat expected for a weighted average of the blended components,demonstrating some positive synergies in the film of the blend. Further,the addition of resin 1A improves optical properties without reducingthe dart impact and MD tear as much as using HPLDPE (e.g., LF-Y819-A) asa blend component in equivalent amounts. Thus, compared to a blendcontaining HPLDPE in the same amount as the first polyethylene copolymer1A, film made from the inventive blend comprising 15 wt % 1A and 85 wt %2C has better MD tear, dart impact and puncture resistance properties. Ablend of resin 1C with 2C in a 15/85 weight percent ratio shows positivesynergy with regard to haze and gloss values, each of which are improvedbeyond that expected for a weighted average of the blended components.The MD and TD tear, as well as the MD and TD modulus of the blend madewith resin 1C and resin 2C in a 15/85 weight percent ratio arecomparable to the values expected according to the Rule of Mixing andare not impacted in a hugely negative way. Further, the addition ofresin 1C improves optical properties without reducing the dart impactand MD tear as much as using HPLDPE (e.g. LF-Y819-A) as a blendcomponent in equivalent amounts. The blends of 1A with 2C or 1C with 2Ccan be extruded with a specific output of 2.38 or 2.44 lb/hour/rpmrespectively at an extruder head pressure of from 4030-4065 psi or3875-3910 psi respectively, which is at least comparable to the blendcomprising equivalent amounts of HPLDPE.

Table 8 shows that a blend of resin 1A with resin 2D (a linear lowdensity polyethylene having a melt index I₂ of 1 g/10 min and a densityof 0.92 g/cm³) in a 15/85 weight percent ratio has TD tear and punctureresistance values which are higher than the weighted average expectedfor the blended components. Blends of resin 1A with resin 2D or resin 1Cwith resin 2D in a 15/85 weight percent ratio also demonstrate positivesynergy in the MD and TD elongation at break, as the values for eachblend are higher than the expected weighted average. The dart impact and1% secant modulus of the blends of resin 1A with resin 2D or resin 1Cwith resin 2D in a 15/85 weight percent ratio are comparable to thevalues expected from the Rule of Mixing. It is also evident thataddition of resin 1A improves optical properties without reducing thedart impact and MD tear as much as does the addition of HPLDPE (e.g.,LF-Y819-A) in equivalent amounts. Similar trends are observed for ablend of 1C with 2D in a 15/85 weight percent ratio. Thus, when comparedto a blend containing HPLDPE in the same amount as the firstpolyethylene copolymer 1A, or 1C, film made from the inventive blendshas much better MD tear, dart impact and puncture resistance properties.The blends of 1A with 2D or 1C with 2D can be extruded with a specificoutput of 2.44 or 2.50 lb/hour/rpm respectively at an extruder headpressure of from 4050-4095 psi or 3655-3970 psi respectively, which isat least comparable to the blend comprising equivalent amounts ofHPLDPE.

Overall, Tables 6-8 show that the films made from the polymer blends andwhich are rich in the second polyethylene copolymer (e.g., 15 wt % of 1Aor 1C/85 wt % of 2A, 2B, 2B*, 2C or 2D) have dart impact values of atleast 250 g/mil, have MD tear strengths of greater than 190 g/mil, an MDtear to TD tear ratio of at least 0.4, an MD or TD secant modulus at 1%strain of at least 130 MPa, a haze of less than 10%, and a gloss at 45°of at least 55. The inventive blends in Tables 6-8 demonstrate a goodbalance of stiffness, toughness and optical properties for use in thefilm applications.

FIG. 8 shows that the use of the first polyethylene copolymer (e.g.,resin 1A) in blends with a linear low density polyethylene material(e.g., resins 2B, 2C or 2D), improves the shear thinning ratio(η*_(0.1)/η*₁₀) as determined by dynamic mechanical analysis, which is ameasure of processability, as the amount of the first polyethylenecopolymer is increased in the blend. The synergy in the shear thinningratio for the inventive blends indicates improvements in melt fracturetendency and hence processability.

FIG. 9, shows how the melt strength (in centiNewtons, cN) of a blendwith a linear low density material (e.g. resins 2B, 2C or 2D) alsoincreases as the amount of first polyethylene copolymer (e.g. resin 1A)is increased in the blend. The improvement can be as much as from 20 to45%, depending on the nature of the first and second polyethylenecopolymer components.

In view of the above data, the resin blends disclosed herein haveimproved optical properties relative to either of the blend componentswhen each is blown into film. See Tables 5, 6, 7 and 8. As shown inTable 6, 7 and 8 blending HPLDPE into a linear low density polyethylenecan also improve optical properties, but this comes at the expense ofother film properties, namely the dart impact value, puncture resistanceand the MD direction tears.

Hence, in some embodiments, the present invention provides polymerblends having good processability which when blown into film affordsgood physical properties, such as impact resistance, puncture strength,tear strength and stiffness, as well as good optical properties.

In addition, use of an equivalent amount of the first polyethylenecopolymer in place of a high pressure linear low density material, leadsto blends having far better MD tear strength, dart impact resistance,and puncture strength without significant loss in other propertiesincluding MD modulus and MD and TD elongation at break.

In view of the forgoing, the first polyethylene copolymers describedherein (e.g. resins 1A-1F) can be used as a highly successfulalternative blend component to a HPLDPE material, in order to alleviatethe processing deficiencies of a linear low density polyethylenematerial (such as for example, those having narrow molecular weightdistributions and/or fractional melt indices) with better retention andbalance of MD and TD film properties than HPLDPE material.

Table 9 shows the film properties of blends which are rich in the firstpolyethylene copolymer instead of the second ethylene copolymer (e.g. 85wt % of 1C/15 wt % of 2B*, 2C or 2D).

TABLE 9 Film Properties (1C Rich Inventive Blends of 1C/2B*, 1C/2C and1C/1D) Inventive Blends 85 wt % 85 wt % 85 wt % 1C/15% 1C/15% 1C/15% wt% 2B* wt % 2C wt % 2D Dart Impact (g/mil) 468 539 464 MD Tear (g/mil)112 129 114 TD Tear (g/mil) 405 449 444 Puncture (J/mm) 37 53 59 1% MDSecant Modulus (MPa) 221 228 222 1% TD Secant Modulus (MPa) 228 229 2182% MD Secant Modulus (MPa) 198 200 195 2% TD Secant Modulus (MPa) 194200 190 MD Tensile Strength (MPa) 52.4 56.1 50.9 TD Tensile Strength(MPa) 42.4 43.1 46.8 MD Elongation at Break (%) 535 547 538 TDElongation at Break (%) 648 689 704 MD Yield Strength (MPa) 11.7 11.711.3 TD Yield Strength (MPa) 11.2 11.5 11.4 MD Elongation at Yield (%)14 14 13 TD Elongation at Yield (%) 15 15 15 Haze (%) 12.8 13.1 13.3Gloss (%) 44 43 42 Cold Seal Strength: SIT (° C.) 117 117 116 MaximumForce (N) 14.1 14.4 15.2 Temperature at Max. Force (° C.) 150 140 150Extruder Pressure (psi) 4025-4060 3820-3865 3785-3820 Specific OutputRate (lb/hr/rpm) 2.56 2.50 2.56 Specific Power (lb/hr/Amp) 2.44 2.562.56 Specific Energy (W/lb/hr) 76.7 74.5 72.9

Table 9 shows that the blends of resin 1C with resin 2B*, resin 1C withresin 2C and resin 1C with resin 2D in a 85/15 weight percent ratio havesimilar dart impact, MD and TD tear, puncture resistance, MD and TDsecant modulus, tensile properties, haze and gloss. The three inventiveblends of 85 wt % of first polyethylene copolymer and 15 wt % of secondpolyethylene copolymer also show similar extrusion parameters in thefilm conversion. Such trends indicate that the film properties andprocessability of the blends which are rich in the first polyethylenecopolymer such as 1C do not change significantly, regardless of the typeof the second copolymer (e.g. a linear low density polyethylene, LLDPE)used in the blends. The first polyethylene copolymer described herein(e.g. resins 1A-1F) can be used with a wide range of second polyethylenecopolymers in blends to achieve a good balance of resin processabilityand physical properties in film applications.

The present invention has been described with reference to certaindetails of particular embodiments thereof. It is not intended that suchdetails be regarded as limitations upon the scope of the inventionexcept insofar as and to the extent that they are included in theaccompanying claims.

What is claimed is:
 1. A polymer blend comprising: a) from about 5 toabout 95 wt % of a first polyethylene copolymer having a density of fromabout 0.916 to about 0.936 g/cm³, a melt index (I₂) of from about 0.1 toabout 2.0 g/10 min, a melt flow ratio (I₂₁/I₂) of from about 32 to about50, a molecular weight distribution (M_(w)/M_(n)) of from about 3.6 toabout 6.5, a reverse comonomer distribution profile as determined byGPC-FTIR, a multimodal TREF profile, a composition distribution breadthindex CDBI₅₀ of from 50 wt % to 75 wt % as determined by TREF and whichfurther satisfies the relationship: (M_(w)/M_(n))≧72[(I₂₁/I₂)⁻¹+10⁻⁶(M_(n))]; and b) from about 95 to about 5 wt % of asecond polyethylene copolymer which is a linear low density polyethylene(LLDPE) different from the first polyethylene copolymer and having adensity of from about 0.910 to about 0.940 g/cm³, a melt index (I₂) offrom about 0.2 to about 5.0 g/10 min, and a melt flow ratio (I₂₁/I₂) ofless than about
 35. 2. The polymer blend of claim 1, wherein the firstpolyethylene copolymer has a δ^(XO) of from about 55° to about 70°;wherein δ^(XO) is the phase angle at which the complex modulus (G*) andthe complex viscosity (η*) are numerically equivalent in a plot of phaseangle vs complex modulus and complex viscosity as determined by dynamicmechanical analysis.
 3. The polymer blend of claim 1, wherein the firstpolyethylene copolymer satisfies the relationship:δ^(XO)≦80.7−(CDBI₅₀)/(M_(w)/M_(n)) at a δ^(XO) of from about 55° toabout 70°; wherein δ^(XO) is the phase angle at which the complexmodulus (G*) and the complex viscosity (η*) are numerically equivalentin a plot of phase angle vs complex modulus and complex viscosity asdetermined by dynamic mechanical analysis.
 4. The polymer blend of claim1, wherein the first polyethylene copolymer satisfies the relationship:δ^(XO)≦83.0−1.25(CDBI₅₀)/(M_(w)/M_(n)); wherein δ^(XO) is the phaseangle at which the complex modulus (G*) and the complex viscosity (η*)are numerically equivalent in a plot of phase angle vs complex modulusand complex viscosity as determined by dynamic mechanical analysis. 5.The polymer blend of claim 1, wherein the first polyethylene copolymerhas a multimodal TREF profile comprising two intensity maxima at elutiontemperatures T(low) and T(high); wherein T(low) is from about 65° C. toabout 85° C., and T(high) is from about 90° C. to about 98° C.
 6. Thepolymer blend of claim 1, wherein the blend comprises from about 5 toabout 50 wt % of the first polyethylene copolymer and from about 95 toabout 50 wt % of the second polyethylene copolymer.
 7. The polymer blendof claim 1, wherein the first polyethylene copolymer has a molecularweight distribution (M_(w)/M_(n)) of from about 4.0 to about 6.0.
 8. Thepolymer blend of claim 1, wherein the first polyethylene copolymer has amelt index (I₂) of from about 0.25 to about 0.80 g/10 min.
 9. Thepolymer blend of claim 1, wherein the first polyethylene copolymer has adensity of from about 0.917 to about 0.927 g/cm³.
 10. The polymer blendof claim 1, wherein the first polyethylene copolymer has a Z-averagemolecular weight distribution (M_(z)/M_(w)) of from about 2.0 to about4.0.
 11. The polymer blend of claim 1, wherein the first polyethylenecopolymer has an amount eluting at a temperature of from about 90° C. toabout 105° C. of from about 5 to about 30 weight percent as determinedby TREF.
 12. The polymer blend of claim 1, wherein the firstpolyethylene copolymer has an amount eluting at a temperature of aboveabout 100° C. of about 0 weight percent as determined by TREF.
 13. Thepolymer blend of claim 1, wherein the second polyethylene copolymer hasa density of from about 0.916 to about 0.930 g/cm³.
 14. The polymerblend of claim 1, wherein the second polyethylene copolymer has a CDBI₅₀of at least about 50 wt %.
 15. The polymer blend of claim 1, wherein thesecond polyethylene copolymer has a molecular weight distribution(M_(w)/M_(n)) of from about 1.7 to about 5.0.
 16. A film structurecomprising a least one layer comprising the polymer blend of claim 1.17. A blown film comprising the polymer blend of claim 1, the filmhaving a haze of less than about 10% and a gloss at about 45° of greaterthan about
 55. 18. A cast film comprising the polymer blend of claim 1,the film having a haze of less than about 10% and a gloss at about 45°of greater than about
 55. 19. A polymer blend comprising: a) from about5 to about 95 wt % of a first polyethylene copolymer having a density offrom about 0.916 to about 0.936 g/cm³, a melt index (I₂) of from about0.1 to about 1.0 g/10 min, a melt flow ratio (I₂₁/I₂) of from about 32to about 50, a molecular weight distribution (M_(w)/M_(n)) of from about3.6 to about 6.5, a reverse comonomer distribution profile as determinedby GPC-FTIR, a multimodal TREF profile, a composition distributionbreadth index CDBI₅₀ of from 50 wt % to 75 wt % as determined by TREFand which further satisfies the relationship:(M_(w)/M_(n))≧72[(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))]; and b) from about 95 to about5 wt % of a second polyethylene copolymer which is a linear low densitypolyethylene (LLDPE) having a density of from about 0.910 to about 0.940g/cm³, a melt index (I₂) of from about 0.2 to about 5.0 g/10 min, and amelt flow ratio (I₂₁/I₂) of less than about
 32. 20. The polymer blend ofclaim 19, wherein the first polyethylene copolymer has a δ^(XO) of fromabout 55° to about 70°; wherein δ^(XO) is the phase angle at which thecomplex modulus (G*) and the complex viscosity (η*) are numericallyequivalent in a plot of phase angle vs complex modulus and complexviscosity as determined by dynamic mechanical analysis.
 21. A filmstructure comprising a least one layer comprising the polymer blend ofclaim
 19. 22. A blown film comprising the polymer blend of claim 19, thefilm having a haze of less than about 10% and a gloss at about 45° ofgreater than about
 55. 23. A cast film comprising the polymer blend ofclaim 19, the film having a haze of less than about 10% and a gloss atabout 45° of greater than about
 55. 24. A polymer blend comprising: a)from about 5 to about 95 wt % of a first polyethylene copolymer having adensity of from about 0.916 to about 0.936 g/cm³, a melt index (I₂) offrom about 0.1 to about 1.0 g/10 min, a melt flow ratio (I₂₁/I₂) of atleast about 30, a molecular weight distribution (M_(w)/M_(n)) of fromabout 3.6 to about 6.5, a reverse comonomer distribution profile asdetermined by GPC-FTIR, a multimodal TREF profile, a compositiondistribution breadth index CDBI₅₀ of from 50 wt % to 75 wt % asdetermined by TREF and which further satisfies the relationship:(M_(w)/M_(n))≧72 [(I₂₁/I₂)⁻¹+10⁻⁶ (M_(n))]; and b) from about 95 toabout 5 wt % of a second polyethylene copolymer which is a linear lowdensity polyethylene (LLDPE) having a density of from about 0.910 toabout 0.940 g/cm³, a melt index (I₂) of from about 0.2 to about 5.0 g/10min, and a melt flow ratio (I₂₁/I₂) of less than about
 35. 25. Thepolymer blend of claim 24, wherein the first polyethylene copolymer hasa δ^(XO) of from about 55° to about 70°; wherein δ^(XO) is the phaseangle at which the complex modulus (G*) and the complex viscosity (η*)are numerically equivalent in a plot of phase angle vs complex modulusand complex viscosity as determined by dynamic mechanical analysis. 26.A film structure comprising a least one layer comprising the polymerblend of claim
 24. 27. A blown film comprising the polymer blend ofclaim 24, the film having a haze of less than about 10% and a gloss ofgreater than about
 55. 28. A cast film comprising the polymer blend ofclaim 24, the film having a haze of less than about 10% and a gloss atabout 45° of greater than about 55.